Novel ZrB2-matrix composites were designed and prepared by in-situ introducing SiC and Zr2[Al(Si)]4C5 simultaneously for the first time. The obtained composites were dense and showed good mechanical properties, especially the strength and toughness, 706 MPa and 7.33 MPa·m1/2, respectively, coupled with high hardness of 21.3 GPa, and stiffness of 452 GPa. SiC and Zr2[Al(Si)]4C5 constituted a reinforcing system with synergistic effects including grain refinement, grain pull-out as well as crack branching, bridging, and deflection. Besides, the oxidation results of the composites showed that the oxidation kinetics followed the parabolic law at 1600 °C, and the oxidation rate constants increased with the increase of Zr2[Al(Si)]4C5 content. The formation and evolution model of the oxidation structure was also investigated, and the oxide scale of the composite exhibited a three-layer structure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.