Polyurethane (PU) foam adhesives were prepared from castor oil as a polyol with isocyanate poly(4,4’-methylene diphenyl isocyanate) (PMDI) using a solvent-free process. The NCO/OH molar ratio used for the preparation of PU foams was 1.5. Water, organosiloxane and dibutyltin dilaurate were used as the blowing agent, surfactant and catalyst, respectively. The ratio of blowing agent and catalyst were adjusted to optimize the properties. The results show that PU foam prepared with 4 wt % of castor oil catalyst and blowing agent has minimal water absorption and maximal volume expansion in the PU foams. FT-IR analysis shows that a urethane bond was formed by the hydroxyl group of castor oil and the –NCO group of isocyanate PMDI. More blowing agent and catalyst could improve the volume expansion ratio and reduce water retention of PU foams. It was found that Moso bamboo charcoal (Phyllostachys pubescens) and China fir wood particle (Cunninghamia lanceolate) composites with setting densities of 500 and 600 kg/m3 can be prepared from optimized castor oil-based PU foam adhesive at 100 °C for 5 min under a pressure of 1.5 MPa. Increasing the amount of bamboo charcoal decreases the equilibrium moisture content, water absorption and internal bonding strength of the composite. Notably, bamboo charcoal composite exhibits excellent dimensional stability. The optimized density and bamboo charcoal percentages of the composite were 500 kg/m3 and 50–100%, respectively. The castor oil-based PU composites containing bamboo charcoal fulfilled the CNS 2215 standards for particleboard. This dimensionally stable, low-density bamboo charcoal composite has high potential to replace current indoor building materials.

Most anticancer drugs cause severe side effect due to the lack of selectivity for cancer cells. In recent years, new strategies of micellar systems, which design for specifically target anticancer drugs to tumors, are developed at the forefront of polymeric science. To improve efficiency of delivery and cancer specificity, considerable emphasis has been placed on the development of micellar systems with passive and active targeting. In this review article, we summarized various strategies of designing multifunctional micellar systems in the purpose of improving delivery efficiency. Micellar systems compose of a multifunctional copolymer or a mixture of two or more copolymers with different properties is a plausible approach to tuning the resulting properties and satisfied various requirements for anticancer drug delivery. It appears that multifunctional micellar systems hold great potential in cancer therapy.

No abstract

The limited availability of fossil resource is causing the urgent need to get renewable chemicals. Solvent liquefaction can convert rice husk into bio‐based chemicals. Rice husk was liquefied in polyhydric alcohol catalyzed by sulfuric acid under atmospheric pressure. The viscosity, residue content, and weight average molecular weight (Mw) of liquefied rice husk were 3089 cps, 23.6% and 4100, respectively. Prolonging the liquefaction time decreased the residue content and increased the average molecular weight. Polyurethane (PU) foams were successfully prepared from the liquefied rice husk with different molar ratios of NCO to OH (NCO/OH). The mechanical properties of PU foams showed that the compressive strength in the vertical direction is higher than that in the horizontal direction. With Increase of the NCO/OH molar ratio from 1.0 to 2.0, compressive strength in the vertical direction of PU foams increased from 70.6 to 114.7 kPa at 10% strain. Thermal analysis results showed that thermal stability of liquefied rice husk‐based PU resins was better than that of fossil‐ and liquefied wood‐ based PU resins. Increasing the NCO/OH molar ratio and inorganic residue of rice husk can help to increase thermal stability. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 135, 45910.