Field-effect transistors (FETs) were fabricated with a thin film of 3,10-ditetradecylpicene, picene-(C14H29)2, formed using either a thermal deposition or a deposition from solution (solution process). All FETs showed p-channel normally-off characteristics. The field-effect mobility, μ, in a picene-(C14H29)2 thin-film FET with PbZr0.52Ti0.48O3 (PZT) gate dielectric reached ~21 cm2 V−1 s−1, which is the highest μ value recorded for organic thin-film FETs; the average μ value (<μ>) evaluated from twelve FET devices was 14(4) cm2 V−1 s−1. The <μ> values for picene-(C14H29)2 thin-film FETs with other gate dielectrics such as SiO2, Ta2O5, ZrO2 and HfO2 were greater than 5 cm2 V−1 s−1, and the lowest absolute threshold voltage, |Vth|, (5.2 V) was recorded with a PZT gate dielectric; the average |Vth| for PZT gate dielectric is 7(1) V. The solution-processed picene-(C14H29)2 FET was also fabricated with an SiO2 gate dielectric, yielding μ = 3.4 × 10−2 cm2 V−1 s−1. These results verify the effectiveness of picene-(C14H29)2 for electronics applications.
In the field of beam physics, two frontier topics have taken center stage due to their potential to enable new approaches to discovery in a wide swath of science. These areas are: advanced, high gradient acceleration techniques, and x-ray free electron lasers (XFELs). Further, there is intense interest in the marriage of these two fields, with the goal of producing a very compact XFEL. In this context, recent advances in high gradient radio-frequency cryogenic copper structure research have opened the door to the use of surface electric fields between 250 and 500 MV m−1. Such an approach is foreseen to enable a new generation of photoinjectors with six-dimensional beam brightness beyond the current state-of-the-art by well over an order of magnitude. This advance is an essential ingredient enabling an ultra-compact XFEL (UC-XFEL). In addition, one may accelerate these bright beams to GeV scale in less than 10 m. Such an injector, when combined with inverse free electron laser-based bunching techniques can produce multi-kA beams with unprecedented beam quality, quantified by 50 nm-rad normalized emittances. The emittance, we note, is the effective area in transverse phase space (x, p x /m e c) or (y, p y /m e c) occupied by the beam distribution, and it is relevant to achievable beam sizes as well as setting a limit on FEL wavelength. These beams, when injected into innovative, short-period (1–10 mm) undulators uniquely enable UC-XFELs having footprints consistent with university-scale laboratories. We describe the architecture and predicted performance of this novel light source, which promises photon production per pulse of a few percent of existing XFEL sources. We review implementation issues including collective beam effects, compact x-ray optics systems, and other relevant technical challenges. To illustrate the potential of such a light source to fundamentally change the current paradigm of XFELs with their limited access, we examine possible applications in biology, chemistry, materials, atomic physics, industry, and medicine—including the imaging of virus particles—which may profit from this new model of performing XFEL science.
A new phenacene-type molecule, [8]phenacene, which is an extended zigzag chain of coplanar fused benzene rings, has been synthesised for use in an organic field-effect transistor (FET). The molecule consists of a phenacene core of eight benzene rings, which has a lengthy π-conjugated system. The structure was verified by elemental analysis, solid-state NMR, X-ray diffraction (XRD) pattern, absorption spectrum and photoelectron yield spectroscopy (PYS). This type of molecule is quite interesting, not only as pure chemistry but also for its potential electronics applications. Here we report the physical properties of [8]phenacene and its FET application. An [8]phenacene thin-film FET fabricated with an SiO2 gate dielectric showed clear p-channel characteristics. The highest μ achieved in an [8]phenacene thin-film FET with an SiO2 gate dielectric is 1.74 cm2 V−1 s−1, demonstrating excellent FET characteristics; the average μ was evaluated as 1.2(3) cm2 V−1 s−1. The μ value in the [8]phenacene electric-double-layer FET reached 16.4 cm2 V−1 s−1, which is the highest reported in EDL FETs based on phenacene-type molecules; the average μ was evaluated as 8(5) cm2 V−1 s−1. The μ values recorded in this study show that [8]phenacene is a promising molecule for transistor applications.
The pressure dependence of the superconducting transition temperature (Tc) and unit cell metrics of tetragonal (NH3)yCs0.4FeSe were investigated in high pressures up to 41 GPa. The Tc decreases with increasing pressure up to 13 GPa, which can be clearly correlated with the pressure dependence of c (or FeSe layer spacing). The Tc vs. c plot is compared with those of various (NH3)yMxFeSe (M: metal atoms) materials exhibiting different Tc and c, showing that the Tc is universally related to c. This behaviour means that a decrease in two-dimensionality lowers the Tc. No superconductivity was observed down to 4.3 K in (NH3)yCs0.4FeSe at 11 and 13 GPa. Surprisingly, superconductivity re-appeared rapidly above 13 GPa, with the Tc reaching 49 K at 21 GPa. The appearance of a new superconducting phase is not accompanied by a structural transition, as evidenced by pressure-dependent XRD. Furthermore, Tc slowly decreased with increasing pressure above 21 GPa, and at 41 GPa superconductivity disappeared entirely at temperatures above 4.9 K. The observation of a double-dome superconducting phase may provide a hint for pursuing the superconducting coupling-mechanism of ammoniated/non-ammoniated metal-doped FeSe.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.