Development of pulsed‐techniques aimed to generate highly ionized target species and high plasma density opens up a new way to tailor composition, structure, and properties of coatings. In this work, TiAlSiN coatings have been deposited at various negative substrate biases (Vs) using deep oscillation magnetron sputtering by sputtering a TiAlSi compound target in Ar/N2 mixtures. The increase in Vs from −30 to −120 V resulted in a decrease in (111)‐preferred orientation and grain size, together with the increase in residual stress and rough morphology. The nc‐TiAlN/a‐Si3N4 nanocomposite structure was obtained in coatings. The highest hardness and Young's modulus reached 42.4 and 495 GPa at −120 V, respectively. However, at −60 V, the coatings with the highest H/E* and H3/E*2 ratios of 0.095 and 0.332 exhibited excellent adhesion with above HF1 level, the lowest coefficient of friction (COF) of 0.35 and specific wear rate of 2.1 × 10−7 mm3 N−1 m−1. Wear mechanism changed from the mixture of severe adhesive, oxidative and abrasive wear to mild oxidative wear to severe oxidative wear. TiAlSiN coatings with high hardness and H/E* and H3/E*2 ratios exhibited the decrease in COF and wear rate due to refined grains in uniform distribution, which well promoted oxide layers formed on sliding contact surface.

Using a dedicated data sample taken in 2018 on the J/ψ peak, we perform a detailed study of the trigger efficiencies of the BESIII detector. The efficiencies are determined from three representative physics processes, namely Bhabha scattering, dimuon production and generic hadronic events with charged particles. The combined efficiency of all active triggers approaches 100% in most cases, with uncertainties small enough not to affect most physics analyses.