In this work, Taguchi design (orthogonal array, OA9) was used for the adhesion investigation of an epoxy insulator to a double base (DB) propellant grain. In this manner three epoxy resins based on diglycidylether bisphenol A (DGEBA) and three polyamine curing agents with an active diluent based on DGEBA were used. Therefore, the effects of resin type, curing agent type with its amount and diluent quantity as main factors were investigated on the single lap shear strength (adhesion strength) and then the results were quantitatively evaluated by the analysis of variance (ANOVA). The data given of ANOVA predicted that the best adhesion strength of 15.584 ± 1.606 MPa was obtained for the optimum conditions of MANA POX-102 as epoxy resin, H-37 as curing agent with 57 phr, ERYSYS GE-30 as diluent with 5 phr. In comparison, practical result of adhesion strength obtained for the optimum conditions was 15.4 ± 0.2 MPa. Also the Pull-off test results on the surface of the DB propellant showed that the maximum adhesion strength (related to the optimal conditions) is 2.64 ± 0.2 MPa.