Silicon has attracted ever‐increasing attention as a high‐capacity anode material in Li‐ion batteries owing to its extremely high theoretical capacity. However, practical application of silicon anodes is seriously hindered by its fast capacity fading as a result of huge volume changes during the charge/discharge process. Here, an interpenetrated gel polymer binder for high‐performance silicon anodes is created through in‐situ crosslinking of water‐soluble poly(acrylic acid) (PAA) and polyvinyl alcohol (PVA) precursors. This gel polymer binder with deformable polymer network and strong adhesion on silicon particles can effectively accommodate the large volume change of silicon anodes upon lithiation/delithiation, leading to an excellent cycling stability and high Coulombic efficiency even at high current densities. Moreover, high areal capacity of ∼4.3 mAh/cm2 is achieved based on the silicon anode using the gel PAA–PVA polymer binder with a high mass loading. In view of simplicity in using the water soluble gel polymer binder, it is believed that this novel binder has a great potential to be used for high capacity silicon anodes in next generation Li‐ion batteries, as well as for other electrode materials with large volume change during cycling.

Despite the high theoretical capacity of lithium-sulfur batteries, their practical applications are severely hindered by a fast capacity decay, stemming from the dissolution and diffusion of lithium polysulfides in the electrolyte. A novel functional carbon composite (carbon-nanotube-interpenetrated mesoporous nitrogen-doped carbon spheres, MNCS/CNT), which can strongly adsorb lithium polysulfides, is now reported to act as a sulfur host. The nitrogen functional groups of this composite enable the effective trapping of lithium polysulfides on electroactive sites within the cathode, leading to a much improved electrochemical performance (1200 mAh g(-1) after 200 cycles). The enhancement in adsorption can be attributed to the chemical bonding of lithium ions by nitrogen functional groups in the MNCS/CNT framework. Furthermore, the micrometer-sized spherical structure of the material yields a high areal capacity (ca. 6 mAh cm(-2)) with a high sulfur loading of approximately 5 mg cm(-2), which is ideal for practical applications of the lithium-sulfur batteries.

Room temperature sodium-ion batteries are of great interest for high-energy-density energy storage systems because of low-cost and natural abundance of sodium. Here, we report a novel phosphorus/graphene nanosheet hybrid as a high performance anode for sodium-ion batteries through facile ball milling of red phosphorus and graphene stacks. The graphene stacks are mechanically exfoliated to nanosheets that chemically bond with the surfaces of phosphorus particles. This chemical bonding can facilitate robust and intimate contact between phosphorus and graphene nanosheets, and the graphene at the particle surfaces can help maintain electrical contact and stabilize the solid electrolyte interphase upon the large volume change of phosphorus during cycling. As a result, the phosphorus/graphene nanosheet hybrid nanostructured anode delivers a high reversible capacity of 2077 mAh/g with excellent cycling stability (1700 mAh/g after 60 cycles) and high Coulombic efficiency (>98%). This simple synthesis approach and unique nanostructure can potentially be applied to other phosphorus-based alloy anode materials for sodium-ion batteries.

Herein, we report a synthesis of highly crumpled nitrogen-doped graphene sheets with ultrahigh pore volume (5.4 cm(3)/g) via a simple thermally induced expansion strategy in absence of any templates. The wrinkled graphene sheets are interwoven rather than stacked, enabling rich nitrogen-containing active sites. Benefiting from the unique pore structure and nitrogen-doping induced strong polysulfide adsorption ability, lithium-sulfur battery cells using these wrinkled graphene sheets as both sulfur host and interlayer achieved a high capacity of ∼1000 mAh/g and exceptional cycling stability even at high sulfur content (≥80 wt %) and sulfur loading (5 mg sulfur/cm(2)). The high specific capacity together with the high sulfur loading push the areal capacity of sulfur cathodes to ∼5 mAh/cm(2), which is outstanding compared to other recently developed sulfur cathodes and ideal for practical applications.

Lithium-sulfur (Li-S) batteries offer theoretical energy density much higher than that of lithium-ion batteries, but their development faces significant challenges. Mesoporous carbon-sulfur composite microspheres are successfully synthesized by combining emulsion polymerization and the evaporation-induced self-assembly (EISA) process. Such materials not only exhibit high sulfur-specific capacity and excellent retention as Li-S cathodes but also afford much improved tap density, sulfur content, and areal capacity necessary for practical development of high-energy-density Li-S batteries. In addition, when incorporated with carbon nanotubes (CNTs) to form mesoporous carbon-CNT-sulfur composite microspheres, the material demonstrated superb battery performance even at a high current density of 2.8 mA/cm(2), with a reversible capacity over 700 mAh/g after 200 cycles.