The best method of hardening of low-value wood is pressing her to the extent of 40-50 %. About 2 times its volume decreases and, respectively, but the output of the modified wood. As hardener can be used on-nofibrillyarnuyu cellulose (NFP) in the form of a 2 % hydrogel magnetically activated. Completely replace the pressing NFP is impossible, since hydrogel has a very small concentration of NFP and receive content over 1 % in relation to dry wood impossible. Technology for producing modified wood involves activation of a 2 % hydrogel magnetization in STEL-49 to obtain the analyte with a potential of 600-800 mV and the pH = 2.5. In a 30 % aqueous urea solution was added 20 % activated hydrogel NFP stabilizer and 15 % the size of the particle board - UREAFORMALDEHYDE oligomer aqueous solution (UFC). The resulting mixture is impregnated with crude wood aspen or birch end under pressure to ensure through impregnation. The content of the mixture in the impregnated wood of 40-60 % by weight of the wood. The impregnated wood is dried with simultaneous compression to the extent of 20-25 %. The resulting wood has a moisture content 6-8 %, the density of 800-900 kg / m3, compressive strength parallel to the grain of 100-150 MPa. Due to the presence of urea loss on fire test is reduced 5 times. Biostability modified wood increases from baseline in 2-3 raza.Posle processing wood according to the procedure described obtained modified wood having a degree of compaction of 15 % birch and 25 % aspen, i.e. Use of the method reduces the degree of compaction is twice as compared with the known method, thus also increasing the yield of the resulting material. Reducing pressing for birch from 30 to 15 % increases the yield of modified wood by 15 %, ie 1 m3 with savings of 0.15 m3, with 1000 m3 -150 m3, When the selling price of the modified birch 30 thousand rubles. 1 m3 for savings of 150x30 = 4500 rubles. Reducing the degree of compaction of the aspen from 50 to 25 % increases the yield of modified wood by 25 %, i.e. 1 m3 with savings of 0.25 m3, with 1000 m3 -250 m3. When the selling price of the modified aspen wood 25 thousand rubles. 1 m3 for savings of 250x25 = 6250 rubles.

The possibility of applying nanocellulose as additive in the production of plywood is considered. This involves its activation by physical methods (ultrasonic treatment and PMF). Increase in the strength of the resulting material by increasing the strength of the adhesive joint is experimentally established. But in this case, the strength of the adhesive joint was higher the strength of birch veneer sheets, veneer pack was amplified with basalt material. Studies have also shown that replacement of the two plies on the basalt fabric beneath the outer layers of plywood, gives an increase in tensile strength by adhesive seam compared to the control sample by 220 %.