Karakteristik Struktur Mikro dan Gugus Fungsi Komposit Silika Sekam Padi dan Aspal

Abstract

Composite of rice husk and asphalt silica was carried out at a ratio of 1: 0.7; 1: 0.8 and 1: 0.9 and heated at 150oC for 3 hours. The characteristics of the phase structure, microstructure, and functional groups were analyzed using X-ray Diffraction (XRD), Scanning Electron Microscopy-Energy Dispersive Spectroscopy (SEM-EDS) and Fourier Transform Infrared (FTIR), physical properties analysis (density, porosity) and mechanics (compressive strength). The XRD results showed that the phase in asphalt silica composites detected amorphous carbon at 2θ = 18º and amorphous silica with the amorphous silica peak shifted from 2θ = 22º to 2θ = 20º. Microstructure analysis shows that cracks and clusters are bigger with grain sizes of 7,742 µm, 8,495 µm and 10,921 µm respectively, and the sample composition shows percentage of silicon (Si), Oxygen (O) and sodium (Na), respectively. decreases and the percentage of carbon (C), sulfur (S) increases. The results of FTIR show that the functional groups of Si-OH, Si-O-Si and Si-O bonds are decreasing and the functional groups of C-H bonds are increasing. The addition of asphalt causes the value of density increases, the value of porosity and compressive strength decreases.

Pengujian Gugus Fungsi Silika Berbasis Sekam Padi Dengan Variasi Suhu & Konsentrasi Cetyltrimethylammonium Bromide Sebagai Bahan Baku Mesoporous Silica

“…Ekstraksi silika sekam padi diperoleh dengan metode alkalis [25]. 50 gram sekam padi yang telah dipreparasi ditambahkan ke dalam 500 ml larutan NaOH 1,5% dan dipanaskan hingga mendidih sambil diaduk.…”

Homogenization of Green SiO2 from Rice Husk Burn through Potassium Hydroxide Solid-Liquid Extraction

“…On the other hand, previous researchers ( [7][8][9]. Kalapathy group on 2001, extracted SiO 2 using 1 N NaOH from the rice husks with the extraction method of two-cycle and result 91% yield [7].…”

Efek Waktu Milling Silika Abu Sekam Padi sebagai Filler Aspal Pen 60/70 terhadap Sifat Fisis dan Sifat Termal

“…Filler berfungsi sebagai pengisi rongga udara pada material sehingga memperkaku lapisan aspal. Filler yang pernah digunakan seperti debu batu kapur, debu dolomite, atau semen Portland [2,3,4].…”

“…Peningkatan bahan aspal dapat dengan menambahkan bahan lain seperti silika sebagai filler pada aspal [11]. Penggunaan komposit silika sekam padi dengan aspal menghasilkan nilai porositas sebesar 10,2%, 10% dan 9,8% [4]. Abu sekam padi sebagai filler aspal menghasilkan nilai titik lembek sebesar 48 ˚C [12].…”

“…Silika sekam padi dengan aspal juga dilakukan dengan perbandingan 1:0; 1 : 0,4; 1 : 0,5, dan 1:0,6 menghasilkan daya serap air sebesar 26%; 3%; 1,7%; dan 1,5% [7]. Penggunaan komposit silika sekam padi dengan aspal juga dilakukan dengan perbandingan massa 1 : 0,7 ; 1 : 0,8 ; 1 : 0,9 menghasilkan nilai porositas sebesar 10,2 %, 10 % dan 9,8 % [4]. Penggunaan serat ijuk juga digunakan dengan penambahan aspal sebesar 0%, 0,5%, 1%, 1,5%, dan 2 % menghasilkan porositas sebesar 13,0 %, 17,8 %, 20,4%, 22,3%, dan 22,9% [14].…”