Morphology of micron-sized monodispersed composite polymer particles produced by seeded polymerization for the dispersion of highly monomer-swollen polymer particles

Abstract

Monodispersed polystyrene (PS)/poly(n-butyl methacrylate) (PBMA) composite particles having 9.4 m in diameter were produced by seeded polymerization for the dispersion of highly n-butyl methacrylate (BMA)-swollen PS particles, and their morphologies were examined. The highly BMAswollen PS particles (about 150 times the weight of the PS seed particles) were prepared by mixing monodispersed 1.8 m-sized PS seed particles and 0.7 m sized BMA droplets prepared with an ultrasonic homogenizer in ethanol/water (1/2, w/w) medium at room temperature. After NaNO aqueous solution as inhibitor was added in the dispersion, the seeded polymerization was carried out at 70°C. In an optical microscopic observation, one or two spherical high contrast regions which consisted mainly of PS were observed inside PS/PBMA composite particles. In the PS domain, there were many fine spherical PBMA domains. Such morphologies were based on the phase separation of PS and PBMA within the homogeneous swollen particles during the seeded polymerization.