Superconductivity in the system [Y0.8Ca0.2](SrBa)Cu3−x(BO3)xO7−δ with 0.1≤x≤0.5

Bustamante, Ángel; Santos, V Luis De Los; Willems, Barbara; Barinotto, H C Víctor; González, Carla; Obradors, X.

doi:10.1016/j.jpcs.2005.10.106

Cited by 3 publications

(3 citation statements)

References 9 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Los resultados obtenidos en este periodo de investigación son publicados en la Revista de Investigación de Física de la UNMSM [44], en la Revista Peruana de Química e Ing. Química de la UNMSM [45][46][47], en la revista de la Sociedad Química del Perú [9,14,[48][49][50], en el Advances in Science and Technology [16], en el Journal of Physics and Chemistry of Solids [51,52], en el Open Journal of Superconductivity [53], en el Japanese Journal of Applied Physics [39] y en el Hyperfine Interactions [54] La investigación de materiales superconductores es una disciplina que requiere de proyectos financiados para poder solventar no sólo la compra de los materiales precursores sino las medidas de caracterización en costosos equipos y para el acceso a la información de trabajos de otros investigadores. Por citar un par de ejemplos, una medida de la susceptibilidad magnética de una muestra de 100 mg en el rango de temperatura de 5 a 100 K usando un magnetómetro con sensor SQUID cuesta aproximadamente 300 Nuevos Soles, 75 euros; el acceso a la literatura científica, significa un costo elevado, medio millón de dólares americanos por año en suscripciones a revistas de investigación.…”

Section: Período 2006 -2011unclassified

Visión retrospectiva de los 14 primeros años de investigación en materiales óxidos cerámicos superconductores en la UNMSM

et al. 2011

View full text Add to dashboard Cite

En abril de 2011 se celebró a nivel mundial los primeros 100 años del descubrimiento de la super- conductividad. La superconductividad ha estado en el foco de la física del estado sólido fundamental, ciencias aplicadas e ingeniería. Hoy en día es posible utilizar los materiales superconductores en una primera generación de dispositivos superconductores y en un futuro cercano en trenes magnéticamente levitados, cables superconductores, computadoras cuánticas, nueva generación de teléfonos móviles, nuevos equipos de resonancia magnética, etc. El grupo de materiales de óxidos cerámicos supercon- ductores perteneciente a la UNMSM hemos estudiado con sumo interés el compuesto superconductor YBa2 Cu3 O7 , investigando la incorporación de distintos cationes y aniones en diversos sitios atómi- cos en la estructura, así también como en derivados de esta estructura, con el fin de comprender sus propiedades estructurales, químicas y superconductoras para proponer nuevos compuestos supercon- ductores. Celebramos la primera centuria del descubrimiento de la superconductividad mediante una visión retrospectiva de nuestros resultados en los primeros 14 años de investigación.

show abstract

Section: Período 2006 -2011unclassified

Visión retrospectiva de los 14 primeros años de investigación en materiales óxidos cerámicos superconductores en la UNMSM

et al. 2011

View full text Add to dashboard Cite

show abstract

“…The trifluoroacetate metal-organic chemical solution deposition (TFA-MO-CSD) method is a low cost route for producing YBCO superconducting films because it does not require vacuum conditions or expensive equipment [1][2][3][4][5][6][7][8][9][10][11][12][13]. This technique was introduced by Gupta et al in 1988 in order to prevent the formation of BaCO 3 [14][15][16][17][18][19][20][21][22][23][24][25][26] during fabrication of YBCO films by following the chemical solution deposition (CSD) method [27]. In fact, in other different CSD routes, BaCO 3 agglomerates at the grain boundaries affecting the critical current density (J C ) of the resulting YBCO films up to a factor of around 10 2 -10 3 [28,29].…”

Section: Introductionmentioning

confidence: 99%

YBa2Cu3O7 films grown onto SrTiO3 and YSZ substrates by chemical solution deposition of trifluoroacetates

et al. 2021

View full text Add to dashboard Cite

We report the preparation and characterization of YBa2Cu3O7 (YBCO) films grown onto SrTiO3 and YSZ substrates by the trifluoroacetates chemical solution deposition method and following sintering with oxygen atmosphere at 860 °C. The X-ray diffraction (XRD) reveals (00ℓ) – oriented crystallites indicating epitaxial growth of the films in the c-direction. Despite granular morphology and the presence of Y2BaCuO5 and CuO as minor secondary phases, the technique shows the successful formation of the superconducting YBCO and preventing the formation of the unwanted BaCO3 phase. Rocking curve measurements of the (005) reflection for the YBCO/SrTiO3 was fitted with one Gaussian function with full width at the half maximum (FWHM) of 0.44° confirming that it consists of YBCO crystallites with different texture. For the sample grown on YSZ, the rocking curve was fitted with two Gaussian functions, one corresponding to the YBCO layer (FWHM = 0.4°) and another to the substrate (FWHM = 0.3°). The magnetic measurements taken in zero field cooling and field cooling modes confirm the formation of the superconducting YBCO with critical temperatures (TC) 91.8 and 85.7 K for the samples grown onto YSZ and SrTiO3, respectively. The critical current density (JC) curves indirectly calculated by using the Bean´s model from the M(T) loops were JC ~ 109 A/cm2 for the sample deposited onto YSZ and JC ~ 107A/cm2 for the YBCO deposited onto SrTiO3. Overall, the difference in TC and JC values between both samples could be related to their difference in oxygen content, porosity, hole concentration per Cu ion and the presence of secondary phases.

show abstract

“…We prepared [Y 0.8 Ca 0.2 ](Ba 0.5 Sr 0.5 ) 2 Cu 3 O 7−δ by sol-gel method. Thus, the research on AC susceptibilities of [Y 0.8 Ca 0.2 ](Ba 0.5 Sr 0.5 ) 2 Cu 3 O 7−δ [18][19][20] would reveal the AC loss mechanism of high Tc superconductors. Here, we report that [Y 0.8 Ca 0.2 ](Ba 0.5 Sr 0.5 ) 2 Cu 3 O 7−δ shows not frequency dependence but field dependence behavior.…”

Section: Introductionmentioning

confidence: 99%

Field-dependent Behavior of AC Susceptibility in [Y 0.8 Ca 0.2](Ba 0.5 Sr 0.5)2 Cu 3 O 7−δ

Lee

Seo

Valladares

et al. 2015

J Supercond Nov Magn

View full text Add to dashboard Cite

The AC susceptibility of [Y 0.8 Ca 0.2 ](Ba 0.5 Sr 0.5 ) 2 Cu 3 O 7−δ was investigated as a function of frequency and amplitude of AC magnetic field. The susceptibilities of the sample display the field amplitude dependence. The peak temperature (T p ) of its imaginary part shows not frequency dependence but field amplitude dependence. The frequency effect on AC susceptibility was negligible. As the field amplitude increases, T p shifts to lower temperature.

show abstract

Superconductivity in the system [Y0.8Ca0.2](SrBa)Cu3−x(BO3)xO7−δ with 0.1≤x≤0.5

Cited by 3 publications

References 9 publications

Visión retrospectiva de los 14 primeros años de investigación en materiales óxidos cerámicos superconductores en la UNMSM

Visión retrospectiva de los 14 primeros años de investigación en materiales óxidos cerámicos superconductores en la UNMSM

YBa2Cu3O7 films grown onto SrTiO3 and YSZ substrates by chemical solution deposition of trifluoroacetates

Field-dependent Behavior of AC Susceptibility in [Y 0.8 Ca 0.2](Ba 0.5 Sr 0.5)2 Cu 3 O 7−δ

Contact Info

Product

Resources

About