Zinc oxide (ZnO) and ZnO : Ga films have been deposited by the spray pyrolysis method onto preheated glass substrates using zinc acetate and gallium nitrate as precursors for Zn and Ga ions, respectively. The effect of Ga doping on the structural, morphological, optical and electrical properties of sprayed ZnO thin films were investigated using x-ray diffraction (XRD), scanning electron microscopy , optical absorption, photoluminescence (PL) and Hall effect techniques. XRD studies reveal that films are polycrystalline with hexagonal (wurtzite) crystal structure. The thin films were oriented along the (0 0 2) plane. Room temperature PL measurements indicate that the deposited films exhibit proper doping of Ga in ZnO lattice. The average transparency in the visible range was around ∼85-95% for typical thin film deposited using 2 at% gallium doping. The optical band gap increased from 3.31 to 3.34 eV with Ga doping of 2 at%. The addition of gallium induces a decrease in electrical resistivity of the ZnO : Ga films up to 2 at% gallium doping. The highest figure of merit observed in this present study was 3.09 × 10 −3 cm 2 −1 .
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.