We recorded X-ray diffraction, 13C CP-MAS NMR, and infrared spectra of silk fibroin samples from Bombyx mori in the solid state, prepared under different conditions, in order to compare conformational features obtained by the respective methods. These three methods provided consistent data as to the presence of the most stable silk II form. Silk I and random-coil forms were distinguishable only by the extent of line broadening in 13C NMR peaks, although the chemical shifts are the same. The most obvious advantage of the 13C CP-MAS NMR approach is that this method is intrinsically nondestructive and very convenient for evaluation of the relative proportion of silk I and II forms in the same sample. We found that powder formation even at liquid-nitrogen temperature caused a change from silk I to random-coil form, although the amount of silk II form remains unchanged during this procedure. In view of the sample preparation conditions as well as the similarity of the 13C chemical shifts and infrared spectra between the silk I and random-coil forms, it is plausible that the random-coil form is a mixture of silk I type forms whose long-range crystalline packing is distorted to the extent to give halo X-ray diffraction.

No abstract

To investigate the influence of bleaching treatments on keratin fibers, the structure of cross-sections at various depths of bleached human hair (black and white human hair) was directly analyzed without isolating the cuticle and cortex, using Raman spectroscopy. The S-S band intensity existing from the cuticle region to the center of cortex region of virgin white human hair decreased, while the S-O band intensity at 1040 cm(-1), assigned to cysteic acid, increased by performing the bleaching treatment. Especially, the S-O band intensity of the cuticle region increased remarkably compared with that of the cortex region. Also, the amide III (unordered) band intensity in the cortex region increased, indicating that some of the proteins existing throughout the cortex region changed to the random coil form. Moreover, it has been found that the S-S band intensity existing from the cuticle region to the center of the cortex region of the virgin black human hair decreased remarkably, while the S-O band intensity increased significantly compared with that of the virgin white human hair by performing the bleaching treatment. From these experiments, we concluded that the melanin granules including metal ions act as a decomposition accelerator for the oxidizing agent, thereby leading to a higher level of disulfide (-SS-) group cleavage in the black human hair compared with that of the white human hair.

In order to investigate the influence of chemical treatments (reduction, heating, and oxidation) on keratin fibers, the structure of virgin white human hair resulting from a permanent hair straightening process at various depths of cross-sectional samples was directly analyzed without isolating the cuticle and cortex, using Raman spectroscopy. The band shape of the cuticle was different from that of the cortex, and the cuticle had a more amorphous structure, compared with the cortex. The S-S band intensity existing in the hair surface remarkably decreased, while the S-S band intensity in the hair center was not changed by performing the reduction process. In the case of heating the keratin fibers after the reduction process, this tendency was unchanged. On the other hand, the amide III (unordered) band intensity in the cortex region increased, indicating that proteins existing throughout the cortex region caused a change to the random coil form. Moreover, approximately 95% of the disconnected -SS- groups were clearly reconnected by performing the oxidation process after heating (the degree of reconnection of -SS- groups was about 90%, in the case of oxidizing after reduction). From these experiments, we concluded that the heat treatment process in the permanent hair straightening treatment caused the randomization of proteins existing throughout the cortex region, thereby contributing to the acceleration of the reconnection of -SS- groups during the oxidation process.

To investigate the mechanism leading to the reduction in tensile strength of permanent waved human hair, the structure of cross-sections at various depths of permanent waved white human hair was directly analyzed without isolating the cuticle and cortex, using Raman spectroscopy. The beta-sheet and/or random coil content (beta/R) and the Amide III(unordered) band intensity existing throughout the cortex region of virgin white human hair remarkably increased, while the alpha-helix (alpha) content slightly decreased by performing the permanent waving treatment. This suggests a secondary structural change from the alpha-helix form to the random coil form in the proteins existing in the microfibril of the cortex region. On the other hand, the S-S band intensity existing in the matrix of the cortex region almost did not change, despite the reduction in the tensile strength of the white human hair following the permanent waving treatment. Moreover, the transmission electron microscope observation shows that the macrofibril (the microfibril and matrix) existing in the cortex region of the virgin white human hair was remarkably disturbed, while the cuticle region was almost unchanged by performing the permanent waving treatment. From these experiments, the authors concluded that some of proteins existing in the cortex region (the microfibril and matrix) of the virgin white human hair were changed, thereby leading to the remarkable reduction in the tensile strength of the white human hair after the permanent waving treatment.