Today, orthopaedics is still in search for the most reliable biomaterial for prosthesis. The biomaterial needs to have good longevity and other supporting properties in order to maintain low implant failure. An ideal metallic biomaterial should be biocompatible, has similar elastic modulus to that of bone, has excellent resistance to fatigue, corrosion, aseptic loosening, and wear, and has good bone-bonding ability. The success of an implant depends on many factors. Good osseointegration is one of the factors required to reduce the rate of loosening of implants and in order to increase the chance of osseointegration, high stability of implants and early healing process encouragement are needed.

PurposeUp to now, there is no feasible solution for stopping or reversing the degenerative process of osteoarthritis (OA). Our study evaluated the effect of intra-articular injection of growth hormone (GH) in OA-induced rabbit knees compared to hyaluronic acid (HA) and placebo.Materials and MethodsA total of 21 male, skeletally mature, New Zealand rabbits received an intra-articular type II collagenase injection for OA induction. Two weeks later, the rabbits were randomized into three groups based on the weekly intra-articular injection to be received: GH, HA, and saline. Injections were done for three consecutive weeks. Evaluation was done at 8 weeks after treatment, clinically using the lameness period, macroscopically using the Yoshimi score and microscopically using the Mankin score.ResultsThe shortest period of lameness was found in the GH group (15.9±2.12 days), compared to the HA group (19.4±1.72 days) and placebo group (25.0±2.94 days). There was a statistically significant difference in macroscopic scoring between groups (p=0.001) in favor of the GH group. There was also significant difference in the microscopic score between groups (p=0.001) also in favor of the GH group.ConclusionsIntra-articular injection of GH showed better clinical, macroscopic and microscopic results as compared to HA and placebo.

Bone reconstructive surgery has become a common procedure, and bone transplantation has become the second most frequently performed tissue transplantation procedure worldwide. Therefore, the need for bone substitute materials has increased. Artificial bone substitutes exhibit osteoconductive properties and feature several advantages, including abundant resources, low cost, and low donor site morbidity. Carbonate apatite (CO3Ap) is a calcium phosphate ceramic that can be used as a synthetic bone graft. The carbonate content of this ceramic is similar to that of bone apatite. In this review, we show that carbonate apatite can be degraded given its chemical reactivity in a weakly acidic environment and through osteoclast resorption. Moreover, it is osteoconductive and promotes bone tissue formation without fibrotic tissue formation. Additionally, microstructural analysis revealed that new bone tissue is formed within the bone graft itself.