Recently, two-dimensional materials such as molybdenum disulphide (MoS2) have been demonstrated to realize field effect transistors (FET) with a large current on-off ratio. However, the carrier mobility in backgate MoS2 FET is rather low (typically 0.5–20 cm2/V·s). Here, we report a novel field-effect Schottky barrier transistors (FESBT) based on graphene-MoS2 heterojunction (GMH), where the characteristics of high mobility from graphene and high on-off ratio from MoS2 are properly balanced in the novel transistors. Large modulation on the device current (on/off ratio of 105) is achieved by adjusting the backgate (through 300 nm SiO2) voltage to modulate the graphene-MoS2 Schottky barrier. Moreover, the field effective mobility of the FESBT is up to 58.7 cm2/V·s. Our theoretical analysis shows that if the thickness of oxide is further reduced, a subthreshold swing (SS) of 40 mV/decade can be maintained within three orders of drain current at room temperature. This provides an opportunity to overcome the limitation of 60 mV/decade for conventional CMOS devices. The FESBT implemented with a high on-off ratio, a relatively high mobility and a low subthreshold promises low-voltage and low-power applications for future electronics.

Hydrogen evolution reaction (HER) from water electrolysis is an attractive technique developed in recent years for cost-effective clean energy. Although considerable efforts have been paid to create efficient catalysts for HER, the development of an affordable HER catalyst with superior performance under mild conditions is still highly desired. In this work, metal-organic frameworks (MOFs)-templated strategy is proposed for in situ coupling of cobalt phosphide (CoP) polyhedrons nanoparticles and carbon nanotubes (CNTs). Due to the synergistic catalytic effect between CoP polyhedrons and CNTs, the as-prepared CoP-CNTs hybrids show excellent HER performance. The resultant CoP-CNTs demonstrate excellent HER activity in 0.5 m H SO with Tafel slope of 52 mV dec , small onset overpotential of ≈64 mV, and a low overpotential of ≈139 mV at 10 mA cm . Additionally, the catalyst also manifests superior durability in acid media. Considering the structure diversity of MOFs, the strategy presented here can be extended for synthesizing other well-defined metal phosphides-CNTs hybrids, which may be used in the fields of catalysis, energy conversion and storage.

The continuous tuning of the emission spectrum of a single light-emitting diode (LED) by an external electrical bias is of great technological significance as a crucial property in high-quality displays, yet this capability has not been demonstrated in existing LEDs. Graphene, a tunable optical platform, is a promising medium to achieve this goal. Here we demonstrate a bright spectrally tunable electroluminescence from blue (∼450 nm) to red (∼750 nm) at the graphene oxide/reduced-graphene oxide interface. We explain the electroluminescence results from the recombination of Poole–Frenkel emission ionized electrons at the localized energy levels arising from semi-reduced graphene oxide, and holes from the top of the π band. Tuning of the emission wavelength is achieved by gate modulation of the participating localized energy levels. Our demonstration of current-driven tunable LEDs not only represents a method for emission wavelength tuning but also may find applications in high-quality displays.