The synthesis and application of carbon-supported, nitrogen-based organometallic silver catalysts for the reduction of CO(2) is studied using an electrochemical flow reactor. Their performance toward the selective formation of CO is similar to the performance achieved when using Ag as the catalyst, but comparatively at much lower silver loading. Faradaic efficiencies of the organometallic catalyst are higher than 90%, which are comparable to those of Ag. Furthermore, with the addition of an amine ligand to Ag/C, the partial current density for CO increases significantly, suggesting a possible co-catalyst mechanism. Additional improvements in activity and selectivity may be achieved as greater insight is obtained on the mechanism of CO(2) reduction and on how these complexes assemble on the carbon support.

We report characterization of a non-precious metal-free catalyst for the electrochemical reduction of CO to CO; namely, a pyrolyzed carbon nitride and multiwall carbon nanotube composite. This catalyst exhibits a high selectivity for production of CO over H (approximately 98 % CO and 2 % H ), as well as high activity in an electrochemical flow cell. The CO partial current density at intermediate cathode potentials (V=-1.46 V vs. Ag/AgCl) is up to 3.5× higher than state-of-the-art Ag nanoparticle-based catalysts, and the maximum current density is 90 mA cm . The mass activity and energy efficiency (up to 48 %) were also higher than the Ag nanoparticle reference. Moving away from precious metal catalysts without sacrificing activity or selectivity may significantly enhance the prospects of electrochemical CO reduction as an approach to reduce atmospheric CO emissions or as a method for load-leveling in relation to the use of intermittent renewable energy sources.

The performance of a novel carbon-supported copper complex of 3,5-diamino-1,2,4-triazole (Cu-tri/C) is investigated as a cathode material using an alkaline microfluidic H(2)/O(2) fuel cell. The absolute Cu-tri/C cathode performance is comparable to that of a Pt/C cathode. Furthermore, at a commercially relevant potential, the measured mass activity of an unoptimized Cu-tri/C-based cathode was significantly greater than that of similar Pt/C- and Ag/C-based cathodes. Accelerated cathode durability studies suggested multiple degradation regimes at various time scales. Further enhancements in performance and durability may be realized by optimizing catalyst and electrode preparation procedures.