The novelty of this study consists in the formulation and characterization of three experimental dental composites (PM, P14M, P2S) for cervical dental lesion restoration compared to the commercial composites Enamel plus HRi® - En (Micerium S.p.A, Avengo, Ge, Italy), G-ænial Anterior® - Ge, (GC Europe N.V., Leuven, Belgium), Charisma® - Ch (Heraeus Kulzer, Berkshire, UK). The physio-chemical properties were studied, like the degree of conversion and the residual monomers in cured samples using FTIR-ATR (attenuated total reflectance) and HPLC-UV (ultraviolet detection), as well as the evaluation of the mechanical properties of the materials. The null hypothesis was that there would be no differences between experimental and commercial resin composites regarding the evaluated parameters. Statistical analysis revealed that water and saliva storage induced significant modifications of all mechanical parameters after three months for all tested materials, except for a few comparisons for each type of material. Storage medium seemed not to alter the values of mechanical parameters in comparison with the initial ones for: diametral tensile strength (DTS-saliva for Ge and PM, compressive strength (CS)-water for Ch, DTS-water and Young’s modulus YM-saliva for P14M and YM-water/ saliva for P2S (p > 0.05). Two of the experimental materials showed less than 1% residual monomers, which sustains good polymerization efficiency. Experimental resin composites have good mechanical properties, which makes them recommendable for the successful use in load-bearing surfaces of posterior teeth.

The clinical performances of dental materials depend on their mechanical profiles, determining their long-term deformation and wear resistance. This paper describes a study on the mechanical properties, water absorption and morphological properties of a polymethyl methacrylate (PMMA) resin enriched with graphene-silver nanoparticles (Gr-Ag). Two different concentrations—1 and 2 wt.%—of Gr-Ag were loaded into the PMMA material. For the mechanical characterization, the compression behavior, flexural strength and tensile strength were evaluated. Optical microscopy in polarized light and scanning electron microscopy were used for filler analysis. The filler addition led to an improvement in all mechanical properties, with slight changes being derived from the filler content variation. Gr-Ag use led to an increase in the applied maximum loads. Moreover, 1 wt.% Gr-Ag determined an increase of 174% in the modulus of rupture, which indicates high flexibility.

No abstract

No abstract

No abstract