Gold (Au) is an interesting catalytic material because of its ability to catalyze reactions, such as partial oxidations, with high selectivities at low temperatures; but limitations arise from the low O2 dissociation probability on Au. This problem can be overcome by using Au nanoparticles supported on suitable oxides which, however, are prone to sintering. Nanoporous Au, prepared by the dealloying of AuAg alloys, is a new catalyst with a stable structure that is active without any support. It catalyzes the selective oxidative coupling of methanol to methyl formate with selectivities above 97% and high turnover frequencies at temperatures below 80 degrees C. Because the overall catalytic characteristics of nanoporous Au are in agreement with studies on Au single crystals, we deduced that the selective surface chemistry of Au is unaltered but that O2 can be readily activated with this material. Residual silver is shown to regulate the availability of reactive oxygen.

Selective electrochemical reduction of CO2 is one of the most sought-after processes because of the potential to convert a harmful greenhouse gas to a useful chemical. We have discovered that immobilized Ag nanoparticles supported on carbon exhibit enhanced Faradaic efficiency and a lower overpotential for selective reduction of CO2 to CO. These electrocatalysts were synthesized directly on the carbon support by a facile one-pot method using a cysteamine anchoring agent resulting in controlled monodispersed particle sizes. These synthesized Ag/C electrodes showed improved activities, specifically decrease of the overpotential by 300 mV at 1 mA/cm(2), and 4-fold enhanced CO Faradaic efficiency at -0.75 V vs RHE with the optimal particle size of 5 nm compared to polycrystalline Ag foil. DFT calculations enlightened that the specific interaction between Ag nanoparticle and the anchoring agents modified the catalyst surface to have a selectively higher affinity to the intermediate COOH over CO, which effectively lowers the overpotential.

No abstract

The Midas touch: The low-temperature transformation of methanol to methyl formate, formaldehyde, and formic acid is promoted by atomic oxygen adsorbed on metallic gold (see picture). The reactions occur with O-containing Au nanoparticles formed on Au(111) upon oxidation with ozone at 200 K; the facile esterification to methyl formate occurs well below room temperature.

Methyl formate is produced from the photo-oxidation of methanol on preoxidized TiO(2)(110). We demonstrate that two consecutive photo-oxidation steps lead to methyl formate using mass spectrometry and scanning tunneling microscopy. The first step in methanol oxidation is formation of methoxy by the thermal dissociation of the O-H bond to yield adsorbed CH(3)O and water. Formaldehyde is produced via hole-mediated oxidation of adsorbed methoxy in the first photochemical step. Next, transient HCO is made photochemically from formaldehyde. The HCO couples with residual methoxy on the surface to yield methyl formate. Exposure of the titania surface to O(2) is required for these photo-oxidation steps in order to heal surface and near-surface defects that can serve as hole traps. Notably, residual O adatoms are not required for photochemical production of methyl formate or formaldehyde. All O adatoms react thermally with methanol to form methoxy and gaseous water at rt, leaving a surface devoid of O adatoms. The mechanism provides insight into the photochemistry of TiO(2) and suggests general synthetic pathways that are the result of the ability to activate both alkoxides and aldehydes using photons.