Quantum dots (QDs) and magnetic nanoparticles (MPs) are of interest for biological imaging, drug targeting, and bioconjugation because of their unique optoelectronic and magnetic properties, respectively. To provide for water solubility and biocompatibility, QDs and MPs were encapsulated within a silica shell using a reverse microemulsion synthesis. The resulting SiO2/MP-QD nanocomposite particles present a unique combination of magnetic and optical properties. Their nonporous silica shell allows them to be surface modified for bioconjugation in various biomedical applications.

The recent discovery of ferromagnetism above room temperature in low-temperature-processed MnO(2)-ZnO has generated significant interest. Using suitably designed bulk and thin-film studies, we demonstrate that the ferromagnetism in this system originates in a metastable phase rather than by carrier-induced interaction between separated Mn atoms in ZnO. The ferromagnetism persists up to approximately 980 K, and further heating transforms the metastable phase and kills the ferromagnetism. By studying the interface diffusion and reaction between thin-film bilayers of Mn and Zn oxides, we show that a uniform solution of Mn in ZnO does not form under low-temperature processing. Instead, a metastable ferromagnetic phase develops by Zn diffusion into the Mn oxide. Direct low-temperature film growth of Zn-incorporated Mn oxide by pulsed laser deposition shows ferromagnetism at low Zn concentration for an optimum oxygen growth pressure. Our results strongly suggest that the observed ferromagnetic phase is oxygen-vacancy-stabilized Mn(2-x)Zn(x)O(3-delta.).

No abstract

We report on the structural, electrical, and optical properties of 5% niobium doped TiO2 thin films grown on various substrates by pulsed laser deposition. The epitaxial anatase Nb:TiO2 film on LaAlO3 is shown to be an intrinsic transparent metal and its metallic property arises from Nb substitution into Ti site as evidenced by the Rutherford backscattering channeling result. In contrast, the rutile Nb:TiO2 thin films show insulating behaviors with 2–3 orders higher room temperature electrical resistivity and ∼30 times lower mobility. A blueshift in the optical absorption edge is observed in both phases, though of differing magnitude.