This study analyzed the relationship between the degree of conversion (DC), solubility, and salivary sorption of a hybrid (Filtek P 60) and a nanofilled resin composite (Filtek Supreme), and evaluated the influence of the light-activation mode on these properties. Two light-activation modes were used: Conventional (C; 850 mW/cm2 for 20 s) and Soft-start (SS; 100-1,000 mW/cm2 for 10 s + 1,000 mW/cm2 for 10 s). The DC (%) was evaluated by FT-Raman spectroscopy. The solubility and salivary sorption were measured after immersion in artificial saliva for 7 days. Data were analyzed by ANOVA and Student-Newman-Keuls' test and linear regression analysis (α = 0.05). The DC varied from 50.52% (nanofilled composite) to 57.15% (hybrid composite), and was influenced by the light-activation mode: C > SS. The solubility (0.45 μg/mm3) and salivary sorption (8.04 μg/mm3) of the nanofilled composite were greater than those of the hybrid composite (0.40 μg/mm3/ 6.87 μg/mm3), and were influenced by the light-activation mode: SS > C. Correlation was found between DC and solubility (r = - 0.89, p<0.05), as well as between solubility and salivary sorption (r = 0.95). These findings suggest that nanofilled composites may present higher degradation in the oral environment than hybrid ones. Soft-start light-activation mode may increase the solubility of resin composites.

This study evaluated the effects of acidic medicines (Dimetapp® and Claritin®), under pH-cycling conditions, on the surface degradation of four composite resins (microhybrid: TPH, Concept, Opallis and Nanofilled: Supreme). Thirty disc-shaped specimens (Ø = 5.0 mm / thickness = 2.0 mm) of each composite were randomly assigned to 3 groups (n = 10): a control and two experimental groups, according to the acidic medicines evaluated. The specimens were finished and polished with aluminum oxide discs, and the surface roughness was measured by using a profilometer. After the specimens were submitted to a pH-cycling regimen and immersion in acidic medicines for 12 days, the surface roughness was measured again. Two specimens for each material and group were analyzed by scanning electron microscopy (SEM) before and after pH-cycling. Data were analyzed by the Student's-t test, ANOVA, Duncan's multiple range test and paired t-test (α=0.05). Significant increase in roughness was found only for TPH in the control group and TPH and Supreme immersed in Claritin® (p<0.05). SEM analyses showed that the 4 composite resins underwent erosion and surface degradation after being subjected to the experimental conditions. In conclusion, although the roughness was slightly affected, the pH-cycling and acidic medicines caused surface degradation of the composite resins evaluated. Titratable acidity seemed to play a more crucial role on surface degradation of composite resins than pH.

Dimetapp(®) (lowest pH and viscosity) and deionized water (control) showed the most pronounced erosive patterns. Klaricid(®) (highest pH and viscosity) presented an in vitro protective effect against acid attacks perhaps due to its mineral content and viscosity.

No abstract

This study analyzed the influence of light polymerization modes on crosslink density (CD) and the degree of conversion (DC) of dental composites. A minifilled hybrid and a nanofilled dental composite were photoactivated with two light polymerization modes: Conventional-850 mW/cm2 for 20 s and Gradual-50 up to 1,000 mW/cm2 for 10 s+1,000 mW/cm2 for 10 s. DC was determined by the use of FT-Raman-spectrometer. A softening test, using Knoop diamond indentation, was carried out at the top and bottom of 2 mm thick dental composite disks, before and after storage in 100% ethanol for 24 h, in order to represent the amount of crosslink density. Data were analyzed by ANOVA and Student-Newman-Keuls' multiple range test (alpha=0.05). The DC was influenced by light polymerization modes, with Gradual mode presenting lower DC. On bottom surfaces, the nanofilled dental composite was more susceptible to softening by ethanol than minifilled hybrid, and gradual light polymerization of nanofilled dental composite resulted in more softening than when conventional light polymerization was used. The results suggest that nanofilled composites are capable undergoing more plasticization if applied in thick increments.