Bondpad cratering, Cu ball bond interface corrosion, IMD (intermetal dielectric) cracking, and uncontrolled post-wirebond staging are the key technical barriers in Cu wire development. This paper discusses the UHAST (unbiased HAST) reliability performance of Cu wire used in fine-pitch BGA package. In-depth failure analysis has been carried out to identify the failure mechanism under various assembly conditions. Obviously green mold compound, low-halogen substrate, optimized Cu bonding parameters, assembly staging time after wirebonding, and anneal baking after wirebonding are key success factors for Cu wire development in nanoelectronic packaging. Failure mechanisms of Cu ball bonds after UHAST test and CuAl IMC failure characteristics have been proposed and discussed in this paper.

Wearout reliability and diffusion kinetics of Au and Pd-coated Cu (PdCu) ball bonds are useful technical information for Cu wire deployment in nanoscale semiconductor device packaging. This paper discusses the HAST (with bias) and UHAST (unbiased HAST) wearout reliability performance of Au and PdCu wires used in fine pitch BGA packages. In-depth failure analysis has been carried out to identify the failure mechanism under various wearout conditions. Intermetallic compound (IMC) diffusion constants and apparent activation energies (Eaa) of both wire types were investigated after high temperature storage life test (HTSL). Au bonds were identified to have faster IMC formation, compared to slower IMC growth of PdCu. PdCu wire was found to exhibit equivalent or better wearout reliability margin compared to conventional Au wire bonds. Failure mechanisms of Au, Cu ball bonds post-HAST and UHAST tests are been proposed, and both Au and PdCu IMC diffusion kinetics and their characteristics are discussed in this paper.

No abstract

No abstract

No abstract