No abstract

Chitosan (CS), a derivative of the naturally occurring biopolymer chitin, is an attractive material for biomedical applications thanks to its biocompatibility, biodegradability, antibacterial properties and ability to enhance cell adhesion and growth compared to other biopolymers. However, the physical and mechanical stability of CS based materials in aqueous solutions is limited and crosslinking agents are required to increase CS performances in a biological environment. In this work, the effect of three highly-biocompatible crosslinkers as genipin (GP), γ-glycidoxypropyltrimethoxysilane (GPTMS), dibasic sodium phosphate (DSP) and a combination of GPTMS and DSP (GPTMS_DSP) on CS physicochemical, thermal, morphological, mechanical properties, swelling and degradation behavior was investigated. Infrared spectroscopy and thermogravimetric analyses confirmed the chemical reaction between CS and the different crosslinkers. CS wettability was enhanced when CS was DSP ionically crosslinked showing contact angle values of about 65° and exhibiting a higher swelling behavior compared to covalently crosslinked films. Moreover, all the crosslinking methods analyzed improved the stability of CS in aqueous media, showed model molecule permeation in time and increased the mechanical properties when compared with non-crosslinked films. The possibility to tailor the final properties of CS scaffolds through crosslinking is a key strategy in applying CS in different biomedical and tissue engineering applications. The obtained results reveal that the optimization of the crosslinking mechanism provides CS membrane properties required in different biomedical applications.

Injectable hydrogels are becoming of increasing interest in the field of tissue engineering thanks to their versatile properties and to the possibility of being injected into tissues or devices during surgery. In peripheral nerve tissue engineering, injectable hydrogels having shear-thinning properties are advantageous as filler of nerve guidance channels (NGCs) to improve the regeneration process. In the present work, gelatin-based hydrogels were developed and specifically designed for the insertion into the lumen of hollow NGCs through a syringe during surgery. Injectable hydrogels were obtained using an agar-gelatin 20:80 weight ratio, (wt/wt) blend crosslinked by the addition of genipin (A/GL_GP). The physicochemical properties of the A/GL_GP hydrogels were analysed, including their injectability, rheological, swelling and dissolution behaviour, and their mechanical properties under compression. The hydrogel developed showed shear-thinning properties and was applied as filler of NGCs. The A/GL_GP hydrogel was tested in vitro using different cell lines, among them Schwann cells which have been used because they have an important role in peripheral nerve regeneration. Viability assays demonstrated the lack of cytotoxicity. In vitro experiments showed that the hydrogel is able to promote cell adhesion and proliferation. Two- and three-dimensional migration assays confirmed the capability of the cells to migrate both on the surface and within the internal framework of the hydrogel. These data show that A/GL_GP hydrogel has characteristics that make it a promising scaffold material for tissue engineering and nerve regeneration. Copyright © 2014 John Wiley & Sons, Ltd.

Chitosan (CS) has been widely used in a variety of biomedical applications, including peripheral nerve repair, due to its excellent biocompatibility, biodegradability, readily availability and antibacterial activity. In this study, CS flat membranes, crosslinked with dibasic sodium phosphate (DSP) alone (CS/DSP) or in association with the γ-glycidoxypropyltrimethoxysilane (CS/GPTMS_DSP), were fabricated with a solvent casting technique. The constituent ratio of crosslinking agents and CS were previously selected to obtain a composite material having both adequate mechanical properties and high biocompatibility.In vitro cytotoxicity tests showed that both CS membranes allowed cell survival and proliferation.Moreover, CS/GPTMS_DSP membranes promoted cell adhesion, induced Schwann cell-like morphology and supported neurite outgrowth from dorsal root ganglia explants.Preliminary in vivo tests carried out on both types of nerve scaffolds (CS/DSP and CS/GPTMS_DSP membranes) demonstrated their potential for: (i) protecting, as a membrane, the site of nerve crush or repair by end-to-end surgery and avoiding post-operative nerve adhesion; (ii) bridging, as a conduit, the two nerve stumps after a severe peripheral nerve lesion with substance loss.A 1cm gap on rat median nerve was repaired using CS/DSP and CS/GPTMS_DSP conduits to further investigate their ability to induce nerve regeneration in vivo. CS/GPTMS_DSP tubes resulted to be more fragile during suturing and, along a 12-week post-operative lapse of time, they detached from the distal nerve stump. On the contrary CS/DSP conduits promoted nerve fiber regeneration and functional recovery, leading to an outcome comparable to median nerve repaired by autograft. 4

Chitosan (CS) membranes obtained by electrospinning are potentially ideal substrates for soft tissue engineering as they combine the excellent biological properties of CS with the extracellular matrix (ECM)-like structure of nanofibrous mats. However, the high amount of acid solvents required to spun CS solutions interferes with the biocompatibility of CS fibres. To overcome this limitation, novel CS based solutions were investigated in this work. Low amount of acidic acid (0.5M) was used and dibasic sodium phosphate (DSP) was introduced as ionic crosslinker to improve nanofibres water stability and to neutralize the acidic pH of electrospun membranes after fibres soaking in biological fluids. Randomly oriented and aligned nanofibres (128±19nm and 140±41nm, respectively) were obtained through electrospinning process (voltage of 30kV, 30μL/min flow rate and temperature of 39°C) showing mechanical properties similar to those of soft tissues (Young Modulus lower than 40MPa in dry condition) and water stability until 7 days. C2C12 myoblast cell line was cultured on CS fibres showing that the aligned architecture of substrate induces cell orientation that can enhance skeletal muscle regeneration.