The cost effective synthesis and patterning of carbon nanomaterials is a challenge in electronic and energy storage devices. Here we report a one-step, scalable approach for producing and patterning porous graphene films with three-dimensional networks from commercial polymer films using a CO 2 infrared laser. The sp 3 -carbon atoms are photothermally converted to sp 2 -carbon atoms by pulsed laser irradiation. The resulting laserinduced graphene (LIG) exhibits high electrical conductivity. The LIG can be readily patterned to interdigitated electrodes for in-plane microsupercapacitors with specific capacitances of 44 mF cm À 2 and power densities of B9 mWcm À 2 . Theoretical calculations partially suggest that enhanced capacitance may result from LIG's unusual ultra-polycrystalline lattice of pentagon-heptagon structures. Combined with the advantage of one-step processing of LIG in air from commercial polymer sheets, which would allow the employment of a roll-to-roll manufacturing process, this technique provides a rapid route to polymer-written electronic and energy storage devices.

Ultrathin transition metal dichalcogenides (TMDCs) of Mo and W show great potential for digital electronics and optoelectronic applications. Whereas early studies were limited to mechanically exfoliated flakes, the large-area synthesis of 2D TMDCs has now been realized by chemical vapor deposition (CVD) based on a sulfurization reaction. The optoelectronic properties of CVD grown monolayer MoS2 have been intensively investigated, but the influence of stoichiometry on the electrical and optical properties has been largely overlooked. Here we systematically vary the stoichiometry of monolayer MoS2 during CVD via controlled sulfurization and investigate the associated changes in photoluminescence and electrical properties. X-ray photoelectron spectroscopy is employed to measure relative variations in stoichiometry and the persistence of MoOx species. As MoS2−δ is reduced (increasing δ), the field-effect mobility of monolayer transistors increases while the photoluminescence yield becomes nonuniform. Devices fabricated from monolayers with the lowest sulfur content have negligible hysteresis and a threshold voltage of ∼0 V. We conclude that the electrical and optical properties of monolayer MoS2 crystals can be tuned via stoichiometry engineering to meet the requirements of various applications.

Iridium-based particles, regarded as the most promising proton exchange membrane electrolyzer electrocatalysts, were investigated by transmission electron microscopy and by coupling of an electrochemical flow cell (EFC) with online inductively coupled plasma mass spectrometry. Additionally, studies using a thin-film rotating disc electrode, identical location transmission and scanning electron microscopy, as well as X-ray absorption spectroscopy have been performed. Extremely sensitive online time-and potential-resolved electrochemical dissolution profiles revealed that Ir particles dissolve well below oxygen evolution reaction (OER) potentials, presumably induced by Ir surface oxidation and reduction processes, also referred to as transient dissolution. Overall, thermally prepared rutile-type IrO particles are substantially more stable and less active in comparison to as-prepared metallic and electrochemically pretreated (E-Ir) analogues. Interestingly, under OER-relevant conditions, E-Ir particles exhibit superior stability and activity owing to the altered corrosion mechanism, where the formation of unstable Ir(>IV) species is hindered. Due to the enhanced and lasting OER performance, electrochemically pre-oxidized E-Ir particles may be considered as the electrocatalyst of choice for an improved low-temperature electrochemical hydrogen production device, namely a proton exchange membrane electrolyzer.

Corrosion resistance of a transition-metal-rich PtCu3/C oxygen reduction reaction (ORR) catalyst as a representative of Pt alloy-based materials has been significantly improved by doping with small amounts of gold (<1 at. %). Transmission electron microscopy imaging shows near-surface segregation of both platinum and gold with the underlying core consisting predominantly of intermetallic PtCu3. The resulting PtAu skin catalyst shows improved resistance against Cu dissolution, as well as against carbon corrosion if compared to its PtCu3 precursor. Also, it exhibits a much higher Pt and carbon stability than a widely used Pt/C standard. Most importantly, the Au doped sample shows a substantial improvement in stability at the elevated temperature (60 degrees C) degradation test (10 000 cycles; 0.4-1.2 Vim) simulating a real PEM fuel cell environment

Gold–copper (Au–Cu) phases were employed already by pre-Columbian civilizations, essentially in decorative arts, whereas nowadays, they emerge in nanotechnology as an important catalyst. The knowledge of the phase diagram is critical to understanding the performance of a material. However, experimental determination of nanophase diagrams is rare because calorimetry remains quite challenging at the nanoscale; theoretical investigations, therefore, are welcomed. Using nanothermodynamics, this paper presents the phase diagrams of various polyhedral nanoparticles (tetrahedron, cube, octahedron, decahedron, dodecahedron, rhombic dodecahedron, truncated octahedron, cuboctahedron, and icosahedron) at sizes 4 and 10 nm. One finds, for all the shapes investigated, that the congruent melting point of these nanoparticles is shifted with respect to both size and composition (copper enrichment). Segregation reveals a gold enrichment at the surface, leading to a kind of core–shell structure, reminiscent of the historical artifacts. Finally, the most stable structures were determined to be the dodecahedron, truncated octahedron, and icosahedron with a Cu-rich core/Au-rich surface. The results of the thermodynamic approach are compared and supported by molecular-dynamics simulations and by electron-microscopy (EDX) observations.