The unique organic/inorganic superabsorbent hydrogels based on xylan and inorganic clay montmorillonite (MMT) were prepared via grafting copolymerization of acrylic acid (AA) and 2-acrylamido-2-methylpropanesulfonic acid (AMPS) withN,N-methylenebisacrylamide (MBA) as a cross-linking agent and potassium persulfate (KPS) as an initiator. The effect of variables on the swelling capacity of the hydrogels, such as the weight ratios of MMT/xylan, MBA/xylan, and AMPS/AA, was systematically optimized. The results indicated that the superabsorbent hydrogels comprised a porous cross-linking structure of MMT and xylan with side chains that carry carboxylate, carboxamide, and sulfate. The hydrogels exhibit the high compressive modulus (E), about 35–55 KPa, and the compression strength of the hydrogels increased with an increment of the MMT content. The effect of various cationic salt solutions (LiCl, CaCl2, and FeCl3) on the swelling has the following order: Li+> Ca2+> Fe3+. Furthermore, the influence of pH values on swelling behaviors showed that the superabsorbent composites retained around 1000 g g−1over a wide pH range of 6.0–10.0. The xylan-based hydrogels with the high mechanical and swelling properties are promising for the applications in the biomaterials area.

No abstract

No abstract

Three lignin–carbohydrate complex (LCC) preparations were isolated to elucidate the variations of chemical linkages during growth in the early development stages of Neosinocalamus affinis bamboo culms.

The lignin-carbohydrate complex (LCC) was isolated from milled wood lignin of 2- and 24-month-old crude bamboo (Neosinocalamus affinis) culms using acetic acid (AcOH) and then characterized. The results have shown that the LCC preparation from 2-month-old bamboo (L2) exhibited a slightly lower molecular weight than the LCC preparation from the 24-month-old bamboo (L24). Further studies using Fourier transform infrared spectroscopy (FT-IR) and heteronuclear single quantum coherence (2D-HSQC) NMR spectra analyses indicate that the LCC preparations included glucuronoarabinoxylan and G-S-H lignin-type with G>S>>H. The content of the S lignin units of LCC in the mature bamboo was always higher than in the young bamboo. Combined with sugar composition analysis, the contents of phenyl glycoside and ether linkages in the L24 preparation were higher than in the L2 preparation; however, there was a reverse relationship of ester LCC bonds in L2 and L24. Lignin–xylan was the main type of LCC linkage in bamboo LCCs. Lignin–lignin linkages in the LCC preparations included β-β, β-5 and β-1 carbon-to-carbon, as well as β-O-4 ether linkages, but β-1 linkages were not present in L2.