A new zwitterionic conjugated polyelectrolyte without free counterions has been used as an electron injection material in polymer light-emitting diodes. Both the efficiency and maximum brightness were considerably improved in comparison with standard Ca cathode devices. The devices showed very fast response times, indicating that the improved performance is, in addition to hole blocking, due to dipoles at the cathode interface, which facilitate electron injection.

In this paper, we demonstrate a double nanoimprinting process that allows the formation of nanostructured polymer heterojunctions of composition and morphology that can be selected independently. We fabricated photovoltaic (PV) devices with extremely high densities (10(14)/mm(2)) of interpenetrating nanoscale columnar features in the active polymer blend layer. The smallest feature sizes are as small as 25 nm on a 50 nm pitch, which results in a spacing of heterojunctions at or below the exciton diffusion length. Photovoltaic devices based on double-imprinted poly((9,9-dioctylfluorene)-2,7-diyl-alt-[4,7-bis(3-hexylthien-5-yl)-2,1,3-benzothiadiazole]-2',2''-diyl) (F8TBT)/ poly(3-hexylthiophene) (P3HT) films are among the best polymer-polymer blend devices reported to date with a power conversion efficiency (PCE, eta(e)) of 1.9%.

No abstract