In this study, water-soluble ammonium polyphosphate- (APP) and methyl trimethoxysilane (MTMS)-modified industrial bamboo residue (IBR)-derived holocellulose nanofibrils (HCNF/APP/MTMS) were used as the raw materials to prepare aerogels in a freeze-drying process. Synthetically modified aerogels were confirmed by Fourier transform infrared spectroscopy, X-ray diffraction, and thermal stability measurements. As-prepared HCNF/APP/MTMS aerogels showed themselves to be soft and flexible. The scanning electron microscopy (SEM) analysis showed that the foam-like structure translates into a 3D network structure from HCNF aerogels to HCNF/APP/MTMS aerogels. The compressive modules of the HCNF/APP/MTMS aerogels were decreased from 38 kPa to 8.9 kPa with a density in the range of 12.04–28.54 kg/m3, which was due to the structural change caused by the addition of APP and MTMS. Compared with HCNF aerogels, HCNF/APP/MTMS aerogels showed a high hydrophobicity, in which the water contact angle was 130°, and great flame retardant properties. The peak of heat release rate (pHRR) and total smoke production (TSP) decreased from 466.6 to 219.1 kW/m2 and 0.18 to 0.04 m2, respectively, meanwhile, the fire growth rate (FIGRA) decreased to 8.76 kW/s·m2. The thermal conductivity of the HCNF/APP/MTMS aerogels was 0.039 W/m·K. All results indicated the prepared aerogels should be expected to show great potential for thermally insulative materials.

Articular cartilage defects, and subsequent degeneration, are prevalent and account for the poor quality of life of most elderly persons; they are also one of the main predisposing factors to osteoarthritis. Articular cartilage is an avascular tissue and, thus, has limited capacity for healing and self-repair. Damage to the articular cartilage by trauma or pathological causes is irreversible. Many approaches to repair cartilage have been attempted with some potential; however, there is no consensus on any ideal therapy. Tissue engineering holds promise as an approach to regenerate damaged cartilage. Since cell adhesion is a critical step in tissue engineering, providing a 3D microenvironment that recapitulates the cartilage tissue is vital to inducing cartilage regeneration. Decellularized materials have emerged as promising scaffolds for tissue engineering, since this procedure produces scaffolds from native tissues that possess structural and chemical natures that are mimetic of the extracellular matrix (ECM) of the native tissue. In this work, we present, for the first time, a study of decellularized scaffolds, produced from avian articular cartilage (extracted from Gallus Gallus domesticus), reseeded with human chondrocytes, and we demonstrate for the first time that human chondrocytes survived, proliferated and interacted with the scaffolds. Morphological studies of the decellularized scaffolds revealed an interconnected, porous architecture, ideal for cell growth. Mechanical characterization showed that the decellularized scaffolds registered stiffness comparable to the native cartilage tissues. Cell growth inhibition and immunocytochemical analyses showed that the decellularized scaffolds are suitable for cartilage regeneration.