We observe a room-temperature low-threshold transition to a coherent polariton state in bulk GaN microcavities in the strong-coupling regime. Nonresonant pulsed optical pumping produces rapid thermalization and yields a clear emission threshold of 1 mW, corresponding to an absorbed energy density of 29 microJ cm-2, 1 order of magnitude smaller than the best optically pumped (In,Ga)N quantum-well surface-emitting lasers (VCSELs). Angular and spectrally resolved luminescence show that the polariton emission is beamed in the normal direction with an angular width of +/-5 degrees and spatial size around 5 microm.
Room temperature electron mobility of 1170cm2∕Vs is obtained in an undoped, lattice-matched, Al0.82In0.18N∕GaN field-effect transistor heterostructure, while keeping a high (2.6±0.3)×1013cm−2 electron gas density intrinsic to the Al0.82In0.18N∕GaN material system. This results in a two-dimensional sheet resistance of 210Ω∕◻. The high mobility of these layers, grown by metal-organic vapor phase epitaxy on sapphire substrate, is obtained thanks to the insertion of an optimized AlN interlayer, reducing the alloy related interface roughness scattering.
We report on the current properties of Al1−xInxN (x ≈ 0.18) layers lattice-matched (LM) to GaN and their specific use to realize nearly strain-free structures for photonic and electronic applications. Following a literature survey of the general properties of AlInN layers, structural and optical properties of thin state-of-the-art AlInN layers LM to GaN are described showing that despite improved structural properties these layers are still characterized by a typical background donor concentration of (1–5) × 1018 cm−3 and a large Stokes shift (∼800 meV) between luminescence and absorption edge. The use of these AlInN layers LM to GaN is then exemplified through the properties of GaN/AlInN multiple quantum wells (QWs) suitable for near-infrared intersubband applications. A built-in electric field of 3.64 MV cm−1 solely due to spontaneous polarization is deduced from photoluminescence measurements carried out on strain-free single QW heterostructures, a value in good agreement with that deduced from theoretical calculation. Other potentialities regarding optoelectronics are demonstrated through the successful realization of crack-free highly reflective AlInN/GaN distributed Bragg reflectors (R > 99%) and high quality factor microcavities (Q > 2800) likely to be of high interest for short wavelength vertical light emitting devices and fundamental studies on the strong coupling regime between excitons and cavity photons. In this respect, room temperature (RT) lasing of a LM AlInN/GaN vertical cavity surface emitting laser under optical pumping is reported. A description of the selective lateral oxidation of AlInN layers for current confinement in nitride-based light emitting devices and the selective chemical etching of oxidized AlInN layers is also given. Finally, the characterization of LM AlInN/GaN heterojunctions will reveal the potential of such a system for the fabrication of high electron mobility transistors through the report of a high two-dimensional electron gas sheet carrier density (ns ∼ 2.6 × 1013 cm−2) combined with a RT mobility μe ∼ 1170 cm2 V−1 s−1 and a low sheet resistance, R ∼ 210 Ω/□.
The authors report room temperature polariton lasing at λ∼345nm in a hybrid AlInN∕AlGaN multiple quantum well microcavity (MQW-MC) containing a GaN∕AlGaN MQW active region, i.e., the achievement under nonresonant optical excitation of coherent light emission of a macroscopic population of polaritons occupying the lowest energy state of the lower polariton branch. This was made possible by taking advantage of the efficient relaxation of polaritons in a MQW-MC exhibiting a large vacuum Rabi splitting ΩVRS=56meV.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.