The study involved measurements of surface tension of liquid binary copper-bismuth alloys with respect to their chemical composition and temperature as well as investigations of the liquid alloy -refractory material -gaseous phase system wettability using usual refractory materials, i.e. aluminium oxide, magnesium oxide and graphite. The experiments were performed with the use of sessile drop method and a high-temperature microscope coupled with a camera and a computer was utilised.Keywords: surface tension, contact angle, wettability, sessile drop method, high-temperature microscope, liquid Cu-Bi alloys W ramach pracy przeprowadzone zostały pomiary napięcia powierzchniowego ciekłych dwuskładnikowych stopów miedzi z bizmutem, w funkcji składu chemicznego i temperatury oraz badania zwilżalności w układzie: ciekły stop-materiał ogniotrwały-faza gazowa z wykorzystaniem typowych materiałów ogniotrwałych, to jest tlenku glinu, tlenku magnezu oraz grafitu. Badania wykonano metodą kropli leżącej, przy użyciu mikroskopu wysokotemperaturowego sprzężonego z kamerą i komputerem.

No abstract

This paper provides an analysis of the results of studies concerning the impact of pressure on the process of copper removal from liquid ferrous alloys by evaporation. The research was conducted in vacuum induction furnace. Iron alloys with 0.509 to 1.518 %wt. Cu content were used for the tests. Kinetics analysis of the examined process was performed for the obtained results and the Speed of the process partial stages was estimated.Keywords: iron alloys, evaporation, vacuum, mass transfer coefficient W prezentowanej pracy przedstawiono wyniki badań nad możliwością usuwania miedzi z ciekłego żelaza na drodze odparowania. Badania realizowano w indukcyjnym piecu próżniowym. Wykorzystano stopy żelaza zawierające od 0.509 do 1.518% mas. Cu. Dla uzyskanych wyników przeprowadzono analizę kinetyczną badanego procesu i oszacowano szybkości jego etapów cząstkowych.

In the paper, results of a study on the effects of deformation conditions (temperature, strain and strain rate) on flow curves, maximum flow stress and corresponding deformation of Cu-Ti alloys with various Ti contents, subjected to hot deformation, are presented. Evaluation of formability of alloys was performed with the use of a Gleeble HDS-V40 thermal-mechanical simulator during uniaxial hot compression at 700 to 900• C, strain rate of 0.1 to 10.0 s −1 and strain of 0 to 1.2 (70%). It was found that within the analysed ranges of temperature, strain rate and strain, Cu-Ti alloys underwent uniform deformation without cracking. The largest deformation resistances were observed for the alloys with the highest Ti contents; their decrease was possible with the temperature raise and the strain rate reduction.Keywords: copper-titanium alloy, hot compression test, plasticity, flow curves W pracy przedstawiono wyniki badań wpływu warunków odkształcenia (temperatura, wielkość i prędkość odkształcenia) na przebieg krzywych płynięcia, wartość maksymalnego naprężenia uplastyczniającego i odpowiadającego mu odkształcenia odkształcanych plastycznie na gorąco stopów Cu-Ti o zróżnicowanej zawartości Ti. Ocenę podatności do kształtowania plastycznego stopów przeprowadzono na symulatorze cieplno-mechanicznym systemu Gleeble HDS-V40 w warunkach jednoosiowego ściskania na gorąco w zakresie temperatury od 700 do 900• C, prędkości odkształcenia od 0.1 do 10.0 s −1 i odkształcenia od 0 do 1.2 (70%). Stwierdzono, że w analizowanych przedziałach temperatury, prędkości i wielkości odkształcenia stopy Cu-Ti odkształcają się w sposób jednorodny bez udziału pękania. Wykazano, że największe opory kształtowania plastycznego towarzyszą stopom o najwyższej zawartości Ti, a ich zmniejszenie jest możliwe poprzez podwyższenie temperatury i obniżenie prędkości odkształcenia.

No abstract