The use of modern structural adhesives provides a lightweight, practical, and high strength joining methodology, which is increasingly being adopted in the automotive and aeronautical sectors, among many others. However, the strict mechanical performance standards that must be met in these applications require a constant search for ways of improving the adhesives’ behavior, which has led to the growing use of reinforcements as a way of improving the capabilities of bonded joints. The aim of this work was, thus, to analyze how the addition of inorganic fillers to the adhesive layer affects a joint’s strength and its failure mechanism. To this end, single lap joint specimens with mild steel and high strength steel substrates were tested, at quasi-static speeds, and with different amounts of glass microspheres reinforcing two different structural adhesives. The experimental results indicated that the addition of glass particles reduced the joint performance for both substrates under study. Furthermore, the failure pattern was found to evolve from adhesive failure to a cohesive type of failure as the amount of glass particles present in the adhesive was increased.

Adhesives are extensively used in the automotive and aeronautical industries as they enable the creation of durable and light weight joints, with exceptional strength to weight ratios. The constant search for the means of adapting the mechanical performance of adhesives to each application has led to the use of several types of fillers to change their properties. Following a study on the effect of inorganic fillers, i.e., hollow glass beads, in the failure mechanisms of single lap joint’s (SLJ), this work focuses on the response of the strength and fracture properties of structural adhesives to this filler. To this end, their tensile strength and mode I fracture properties were thoroughly analyzed by performing bulk tensile and double-cantilever beam (DCB) tests, at a quasi-static speed. The specimens were manufactured by adding different %v/v of filler to two epoxy-based crash resistant adhesives. Both adhesives have shown a negligible effect on the tensile strength, a decrease in strain at failure and critical energy release rate in mode I, as well as an increase of the Young’s modulus, for higher % in volume of hollow glass beads. These phenomena were further analyzed recurring to scanning electron microscopy, and the concept of rule of mixtures.