Visibly transparent near-UV dye (Exalite 377E)-doped silica in the form of parallelepiped were prepared by the low-temperature sol-gel process. The laser output performance of dye-doped sol-gel silica samples pumped by a short pulse (1 ns) N2 laser at 337 nm was reported. With a grating as the wavelength selection element, the laser was tuned from 367 to 387 nm with a laser linewidth of 2 nm. Using a resonator cavity consisting of two flat mirrors, the sol-gel laser showed a slope efficiency of 34.7% and a pump energy threshold of 20 μJ. The variation of sol-gel laser energy output as a function of the number of pulses under repetitive N2 laser excitation was investigated. The laser output energy decreased initially with the number of shots. The output energy recovered to its original intensity after a ten minute interruption in pumping. In this way, the dye-doped samples showed no signs of long term degradation after being irradiated at 337 nm for tens of thousand shots.
Der elektronenmikroskopische Beugungskontrast von spharischen Einschlussen nalie einer kraftefreien Folienoberflache wird berechnet und mit Hilfe der Theorie der modifizierten Bloch-Wellen kritisch diskutiert. Es wird gezeigt, daB der sogcnannte Schwarz-U'eilJKontrast (S-W-Kontrast) auf zwei Ursachen beruht : ,,Interbandstreuung" zwischen den niodifizierten Bloch-Wellen und ,,Randbedingungen", denen die Elektronenwellen an den Folienoberflachengeniigen miissen. I n Ubereinstimmung mit McIntyre und Brown [12] finden wir, dal3 bei Einschliissen mit hinreichend starker Verzerrung der umgebenden Matrix die ..Tiefenoszillationen" des S-1%' -Kontrastes unterdriickt werden. Es wird gezeigt, daB dieser Effekt unmittelbar auf Besonderheiten des Verschiebungsfeldes eines Einschlusses in der Nahe einer kraftefreien Oberflache zuriickzufuhren ist.The diffraction contrast for electron transmission microscopy is calculated for spherical inclusions that are located close to a traction-free foil surface. The results are discussed in terms of modified Rloch waves. It is demonstrated that the so-called "black-white contrast" can arise either from "interband scattering" between the modified Bloch waves or from the "boundary conditions" for the electron waves a t the foil surfaces. I n agreement with McIntyre and Brown [12], the "depth oscillations" of the black-white contrast are found to be suppressed if the lattice distortion, caused by the inclusion. exceeds a critical value. It is demonstrated that this suppression of the depth oscillation is directly related to special properties of the displacement field of an inclusion near a traction-free surface.
Die Keimbildung von Stapelfehlertetraedern in abgeschrecktem Gold wird auf Grund eines Modells erkliirt, wonach die Keime durch einen DreierstoO von Einfach-, Doppel-und Dreifachleerstellen gebildet werden. Die Keime wirken nach ihrer Bildung als effektive Senken fur die beweglichen Leerstellen. Es werden Gleichungen fur die Variation der Tetraederdichte mit Leerstellenkonzentration und Temperatur und fur die Kinetik der Keimbildung gegeben. Ein quantitativer Vergleich zwischen Theorie und Experiment ergibt itls Bindungsenergie und als Assoziationsentropie von Dreifachleerstellen 0,3 eV bzw. 3,5 k.Die Vierfach-und Funffachleerstellen sind wahrscheinlich instabil, wiihrend die Wanderungsenergie der Dreifachleerstellen vermutlich zwischen den entsprechenden Energien der Einfach-und der Doppelleerstellen liegt.The nucleation of stacking-fault tetrahedra in quenched gold is explained on the basis of a model which suggests that the nuclei are formed by collisions involving single, double, and triple vacancies. After their formation, the nuclei act as sinks for mobile vacancies. Equations are given a) for the dependence of the tetrahedral density on vacancy concentration and temperature and b) for the kinetics of the nuclei. A quantitative comparison between theory and experiments yields values of 0.3 eV and 3.5 k for the binding energy and the association entropy of trivacancies, respectively. The four-fold and five-fold vacancies are probably unstable. The migration energy of the trivacancies probably lies between the migration energies of single and divacancies. EinleitungDie durch Abschrecken in k.f .z. Metallen in Obergleichgewichtskonzentration C eingefrorenen Leerstellen kijnnen sich zu Leerstellenagglomeraten zusammenlagern. Ober die Keimbildungsmechanismen solcher Leerstellenagglomerate ist bis jetzt jedoch nur wenig bekannt. De Jong und Koehler [l] haben als erste versucht, eine quantitative Beschreibung der Keimbildung von Stapelfehlertetraedern zu geben. Danach sollen Vierfachleerstellen L,,) die stabilen Keime sein, die sich spater durch weitere Anlagerung von Leerstellen in Tetraeder umwandeln konnen. In diesem Modell werden die L, durch die Anlagerung einer L, an eine & gebildet, wahrend die Diffusion von Fehlstellen mit eineni lokalen Gleichgewicht zwischen L, und L, beschrieben wird. Das setzt voraus, daB die Bindungsenergie B, von L, klein ist, z. B. B, = 0,l eV. Das Modell ~ 1) Dissertation TH Stuttgart 1965 (Teil 11). 2) Wir fuhren folgende Abkurzungen ein: L, bezeichnet die n-fachen Leerstellen (2. B. L, = Einfachleerstelle); C, deren Konzentration; W, und D, sind die Wanderungsenergie bzw. der Diffusionskoeffizient von L,; AS, ist die Assoziationsentropie und B, dieBindungsenergie von L,. B, entspricht dem Energiegewinn beim Zusammenlagern von n L , zu L,, AS, der dabei auftretenden Anderung der Entropie (ohne Anordnungsentropie). 4, Der Faktor 8 in p gilt fiir L, mit der Form eines gleichseitigen Dreiecks. Fur andere Formen der L, sind andere Zahlenfaktoren malgebend, doch kann man sich gegebenen...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.