In this study, three-dimensional (3D) biopolymeric scaffolds made from collagen, silk fibroin and chitosan were successfully prepared by the freeze drying method. Dialdehyde starch (DAS) was used as a cross-linking agent for the materials. The properties of the materials were studied using density and porosity measurements, scanning electron microscope (SEM) imaging, swelling and moisture content measurements. Additionally, cytocompatibility of the materials in contact with MG-63 osteoblast-like cells was tested by live/dead staining and resazurin reduction assay on days 1, 3 and 7. It was found that new 3D materials made from collagen/silk fibroin/chitosan binary or ternary mixtures are hydrophilic with a high swelling ability (swelling rate in the range of 1680–1900%). Cross-linking of such biopolymeric materials with DAS increased swelling rate up to about 2100%, reduced porosity from 96–97% to 91–93%, and also decreased density and moisture content of the materials. Interestingly, presence of DAS did not influence the microstructure of the scaffolds as compared to non-cross-linked samples as shown by SEM. All the tested samples were found to be cytocompatible and supported adhesion and growth of MG-63 cells as shown by live–dead staining and metabolic activity test.

Superparamagnetic iron oxide nanoparticles (SPIONs) are promising drug delivery carriers and hyperthermia agents for the treatment of cancer. However, to ensure their safety in vivo, SPIONs must be modified in order to prevent unwanted iron release. Thus, SPIONs were coated with silica layers of different morphologies: non-porous (@SiO2), mesoporous (@mSiO2) or with a combination of non-porous and mesoporous layers (@SiO2@mSiO2) deposited via a sol–gel method. The presence of SiO2 drastically changed the surface properties of the nanoparticles. The zeta potential changed from 19.6 ± 0.8 mV for SPIONs to −26.1 ± 0.1 mV for SPION@mSiO2. The Brunauer–Emmett–Teller (BET) surface area increased from 7.54 ± 0.02 m2/g for SPIONs to 101.3 ± 2.8 m2/g for SPION@mSiO2. All types of coatings significantly decreased iron release (at least 10 fold as compared to unmodified SPIONs). SPIONs and SPION@mSiO2 were tested in vitro in contact with human lung epithelial cells (A549 and BEAS-2B). Both nanoparticle types were cytocompatible, although some delay in proliferation was observed for BEAS-2B cells as compared to A549 cells, which was correlated with increased cell velocity and nanoparticles uptake.

The suitability of hydrogel biomaterials for bone regeneration can be improved by incorporation of an inorganic phase in particle form, thus maintaining hydrogel injectability. In this study, carbonate microparticles containing different amounts of calcium (Ca) and magnesium (Mg) were added to solutions of the anionic polysaccharide gellan gum (GG) to crosslink GG by release of Ca and Mg from microparticles and thereby induce formation of hydrogel-microparticle composites. It was hypothesized that increasing Mg content of microparticles would promote GG hydrogel formation. The effect of Mg incorporation on cytocompatibility and cell growth was also studied. Microparticles were formed by mixing Ca and Mg and [Formula: see text] ions in varying concentrations. Microparticles were characterized physiochemically and subsequently mixed with GG solution to form hydrogel-microparticle composites. The elemental Ca:Mg ratio in the mineral formed was similar to the Ca:Mg ratio of the ions added. In the absence of Mg, vaterite was formed. At low Mg content, magnesian calcite was formed. Increasing the Mg content further caused formation of amorphous mineral. Microparticles of vaterite and magnesium calcite did not induce GG hydrogel formation, but addition of Mg-richer amorphous microparticles induced gelation within 20 min. Microparticles were dispersed homogeneously in hydrogels. MG-63 osteoblast-like cells were cultured in eluate from hydrogel-microparticle composites and on the composites themselves. All composites were cytocompatible. Cell growth was highest on composites containing particles with an equimolar Ca:Mg ratio. In summary, carbonate microparticles containing a sufficient amount of Mg induced GG hydrogel formation, resulting in injectable, cytocompatible hydrogel-microparticle composites.

Hydrogels offer several advantages as biomaterials for bone regeneration, including ease of incorporation of soluble substances such as mineralization-promoting enzymes and antibacterial agents. Mineralization with calcium phosphate (CaP) increases bioactivity, while antibacterial activity reduces the risk of infection. Here, gellan gum (GG) hydrogels were enriched with alkaline phosphatase (ALP) and/or Seanol(®), a seaweed extract rich in phlorotannins (brown algae-derived polyphenols), to induce mineralization with CaP and increase antibacterial activity, respectively. The sample groups were unmineralized hydrogels, denoted as GG, GG/ALP, GG/Seanol and GG/Seanol/ALP, and hydrogels incubated in mineralization medium (0.1 M calcium glycerophosphate), denoted as GG/ALP_min, GG/Seanol_min and GG/Seanol/ALP_min. Seanol(®) enhanced mineralization with CaP and also increased compressive modulus. Seanol(®) and ALP interacted in a non-covalent manner. Release of Seanol(®) occurred in a burst phase and was impeded by ALP-mediated mineralization. Groups GG/Seanol and GG/ALP/Seanol exhibited antibacterial activity against methicillin-resistant Staphylococcus aureus. GG/Seanol/ALP_min, but not GG/Seanol_min, retained some antibacterial activity. Eluates taken from groups GG/ALP_min, GG/Seanol_min and GG/ALP/Seanol_min displayed comparable cytotoxicity towards MG-63 osteoblast-like cells. These results suggest that enrichment of hydrogel biomaterials with phlorotannin-rich extracts is a promising strategy to increase mineralizability and antibacterial activity.