The authors report on AlAs∕GaAs micropillar cavities with unprecedented quality factors based on high reflectivity distributed Bragg reflectors (DBRs). Due to an increased number of mirror pairs in the DBRs and an optimized etching process record quality (Q) factors up to 165.000 are observed for micropillars with diameters of 4μm. Optical studies reveal a very small ellipticity of 5×10−4 of the pillar cross section. Because of the high Q factors, strong coupling with a vacuum Rabi splitting of 23μeV is observed for micropillars with a diameter of 3μm.

Results obtained by an advanced growth of site-controlled quantum dots (SCQDs) on pre-patterned nanoholes and their integration into both photonic resonators and nanoelectronic memories are summarized. A specific technique has been pursued to improve the optical quality of single SCQDs. Quantum dot (QD) layers have been vertically stacked but spectrally detuned for single SCQD studies. Thereby, the average emission linewidth of single QDs could be reduced from 2.3 meV for SCQDs in a first QD layer close to the etched nanoholes down to 600 microeV in the third InAs QD layer. Accurate SCQD nucleation on large QD distances is maintained by vertical strain induced QD coupling throughout the QD stacks. Record narrow linewidths of individual SCQDs down to approximately 110 microeV have been obtained. Experiments performed on coupled photonic SCQD-resonator devices show an enhancement of spontaneous emission. SCQDs have also been integrated deterministically in high electron mobility heterostructures and flash memory operation at room temperature has been observed.

We report on a scalable fabrication technology for devices based on single quantum dots (QDs) which combines site-controlled growth of QDs with an accurate alignment procedure. Placement of individual QDs and corresponding device structures with a standard deviation of around 50nm from the target position was achieved. The potential of the technology is demonstrated by fabricating arrays of mesas, each containing one QD at a defined position. The presence of single, optically active QDs in the mesas was probed by scanning microphotoluminescence of the mesa arrays.

Controlled non-local energy and coherence transfer enables light harvesting in photosynthesis and non-local logical operations in quantum computing. This process is intuitively pictured by a pair of mechanical oscillators, coupled by a spring, allowing for a reversible exchange of excitation. On a microscopic level, the most relevant mechanism of coherent coupling of distant quantum bits—like trapped ions, superconducting qubits or excitons confined in semiconductor quantum dots—is coupling via the electromagnetic field. Here we demonstrate the controlled coherent coupling of spatially separated quantum dots via the photon mode of a solid state microresonator using the strong exciton–photon coupling regime. This is enabled by two-dimensional spectroscopy of the sample’s coherent response, a sensitive probe of the coherent coupling. The results are quantitatively understood in a rigorous description of the cavity-mediated coupling of the quantum dot excitons. This mechanism can be used, for instance in photonic crystal cavity networks, to enable a long-range, non-local coherent coupling.

No abstract