Purpose The aim of this paper is to evaluate using statistical methods how two soldering techniques – the convection reflow and vapour phase reflow with vacuum – influence reduction of voids in lead-free solder joints under Light Emitted Diodes (LEDs) and Ball Grid Arrays (BGAs). Design/methodology/approach Distribution of voids in solder joints under thermal and electrical pads of LEDs and in solder balls of BGAs assembled with convection reflow and vapour phase reflow with vacuum has been investigated in terms of coverage or void contents, void diameters and number of voids. For each soldering technology, 80 LEDs and 32 solder balls in BGAs were examined. Soldering processes were carried out in the industrial or semi-industrial environment. The OM340 solder paste of Innolot type was used for LED soldering. Voidings in solder joints were inspected with a 2D X-ray transmission system. OriginLab was used for statistical analysis. Findings Investigations supported by statistical analysis showed that the vapour phase reflow with vacuum decreases significantly void contents and number and diameters of voids in solder joints under LED and BGA packages when compared to convection reflow. Originality/value Voiding distribution data were collected on the basis of 2D X-ray images for test samples manufactured during the mass production processes. Statistical analysis enabled to appraise soldering technologies used in these processes in respect of void formation.

Purpose The purpose of the paper is to experimentally evaluate the impact of voids on thermal conductivity of a macro solder joint formed between a copper cylinder and a copper plate by using reflow soldering. Design/methodology/approach A model of a surface mount device (SMD) was developed in the shape of a cylinder. A copper plate works as a printed circuit board (PCB). The resistor was connected to a power supply and the plate was cooled by a heat sink and a powerful fan. A macro solder joint was formed between a copper cylinder and a copper plate using reflow soldering and a lead-free solder paste SAC305. The solder paste was printed on a plate through stencils of various apertures. It was expected that various apertures of stencils will moderate the various void contents in solder joints. K-type thermocouples mounted inside cylinders and at the bottom of a plate underneath the cylinders measured the temperature gradient on both sides of the solder joint. After finishing the temperature measurements, the cylinders were thinned by milling to thickness of about 2 mm and then X-ray images were taken to evaluate the void contents. Finally the tablets were cross-sectioned to enable scanning electron microscopy (SEM) observations. Findings There was no clear dependence between thermal conductivity of solder joints and void contents. The authors state that other factors such as intermetallic layers, microcracks, crystal grain morfologyof the interface between the solder and the substrate influence on thermal conductivity. To support this observation, further investigations using metallographic methods are required. Originality/value Results allow us to assume that the use of SAC305 alloy for soldering of components with high thermal loads is risky. The common method for thermal balance calculation is based on the sum of serial thermal resistances of mechanical compounds. For these calculations, solder joints are represented with bulk SAC305 thermal conductivity parameters. Thermal conductivity of solder joints for high density of thermal energy is much lower than expected. Solder joints’ structure is not fully comparable with bulk SAC305 alloy. In experiments, the average value of the solder joint conductivity was found to be 8.1 W/m·K, which is about 14 per cent of the nominal value of SAC305 thermal conductivity.

Purpose This paper aims to investigate voiding phenomena in solder joints under thermal pads of light-emitting diodes (LEDs) assembled in mass production environment by reflow soldering by using seven low-voiding lead-free solder pastes. Design/methodology/approach The solder pastes investigated are of SAC305 type, Innolot type or they are especially formulated by the manufacturers on the base of (SnAgCu) alloys with addition of some alloying elements such as Bi, In, Sb and Ti to provide low-void contents. The SnPb solder paste – OM5100 – was used as a benchmark. The solder paste coverage of LED solder pads was chosen as a measure of void contents in solder joints because of common usage of this parameter in industry practice. Findings It was found that the highest coverage and, related to it, the least void contents are in solder joints formed with the pastes LMPA-Q and REL61, which are characterized by the coverage of mean value 93.13% [standard deviation (SD) = 2.72%] and 92.93% (SD = 2.77%), respectively. The void diameters reach the mean value equal to 0.061 mm (SD = 0.044 mm) for LMPA-Q and 0.074 mm (SD = 0.052 mm) for REL61. The results are presented in the form of histograms, plot boxes and X-ray images. Some selected solder joints were observed with 3D computer tomography. Originality/value The statistical analyses are carried out on the basis of 2D X-ray images with using Origin software. They enable to compare features of various solder pastes recommended by manufacturers as low voiding. The results might be useful for solder paste manufacturers or electronic manufacturing services.

No abstract