No abstract

No abstract

Gamma irradiation is able to affect various structural and biological properties of biomaterials In this study, a composite of Hap/PLGA-PEG and their ingredients were submitted to gamma irradiation doses of 25 and 50 KGy. Various properties such as molecular weight (GPC), thermal behavior (DSC), wettability (contact angle), cell viability (MTT assay), and alkaline phosphatase activity were studied for the composites and each of their ingredients. The results showed a decrease in molecular weight of copolymer with no change in the glass transition and melting temperatures after gamma irradiation. In general gamma irradiation can increase the activation energy ΔH of the composites and their ingredients. While gamma irradiation had no effect on the wettability of copolymer samples, there was a significant decrease in contact angle of hydroxyapatite and composites with increase in gamma irradiation dose. This study showed an increase in biocompatibility of hydroxyapatite with gamma irradiation with no significant effect on cell viability in copolymer and composite samples. In spite of the fact that no change occurred in alkaline phosphatase activity of composite samples, results indicated a decrease in alkaline phosphatase activity in irradiated hydroxyapatites. These effects on the properties of PLGA-PEG-hydroxyapatite can enhance the composite application as a biomaterial.

Replacement of peripheral nerve autografts with tissue engineered nerve grafts will potentially resolve the lack of nerve tissue especially in patients with severe concomitant soft tissue injuries. This study attempted to fabricate a tissue engineered nerve graft composed of electrospun PCL conduit filled with collagen‐hyaluronic acid (COL‐HA) sponge with different COL‐HA weight ratios including 100:0, 98:2, 95:5 and 90:10. The effect of HA addition on the sponge porosity, mechanical properties, water absorption and degradation rate was assessed. A good cohesion between the electrospun PCL nanofibers and COL‐HA sponges were seen in all sponges with different HA contents. Mechanical properties of PCL nanofibrous layer were similar to the rat sciatic nerve; the ultimate tensile strength was 2.23 ± 0.35 MPa at the elongation of 35%. Additionally, Schwann cell proliferation and morphology on three dimensional (3D) composite scaffold were evaluated by using MTT and SEM assays, respectively. Rising the HA content resulted in higher water absorption as well as greater pore size and porosity, while a decrease in Schwann cell proliferation compared to pure collagen sponge, although reduction in cell proliferation was not statistically significant. The lower Schwann cell proliferation on the COL‐HA was attributed to the greater degradation rate and pore size of the COL‐HA sponges. Also, dorsal root ganglion assay showed that the engineered 3D construct significantly increases axon growth. Taken together, these results suggest that the fabricated 3D composite scaffold provide a permissive environment for Schwann cells proliferation and maturation and can encourage axon growth.

The oxygen release pattern of CaO2 nanoparticles was biphasic: an initial burst phase for the first 24 hours followed by a descending release rate for three days. The oxygen release rate in the second phase mainly depended on the shrinking-core model for CaO2 hydrolysis.