Deep UV-LEDs (DUV-LEDs) emitting at 233 nm with an emission power of (1.9 ± 0.3) mW and an external quantum efficiency of (0.36 ± 0.07) % at 100 mA are presented. The entire DUV-LED process chain was optimized including the reduction of the dislocation density using epitaxially laterally overgrown AlN/sapphire substrates, development of vanadium-based low resistance n-metal contacts, and employment of high thermally conductive AlN packages. Estimated device lifetimes above 1500 h are achieved after a burn-in of 100 h. With the integration of a UV-transparent lens, a strong narrowing of the far-field pattern was achieved with a radiant intensity of 3 mW/sr measured at 20 mA.

We report on the performance of AlGaN-based deep ultraviolet light-emitting diodes (UV-LEDs) emitting at 265 nm grown on stripe-patterned high-temperature annealed (HTA) epitaxially laterally overgrown (ELO) aluminium nitride (AlN)/sapphire templates. For this purpose, the structural and electro-optical properties of ultraviolet-c light-emitting diodes (UVC-LEDs) on as-grown and on HTA planar AlN/sapphire as well as ELO AlN/sapphire with and without HTA are investigated and compared. Cathodoluminescence measurements reveal dark spot densities of 3.5 × 10 9    cm − 2 , 1.1 × 10 9    cm − 2 , 1.4 × 10 9    cm − 2 , and 0.9 × 10 9    cm − 2 in multiple quantum well samples on as-grown planar AlN/sapphire, HTA planar AlN/sapphire, ELO AlN/sapphire, and HTA ELO AlN/sapphire, respectively, and are consistent with the threading dislocation densities determined by transmission electron microscopy (TEM) and high-resolution X-ray diffraction rocking curve. The UVC-LED performance improves with the reduction of the threading dislocation densities (TDDs). The output powers (measured on-wafer in cw operation at 20 mA) of the UV-LEDs emitting at 265 nm were 0.03 mW (planar AlN/sapphire), 0.8 mW (planar HTA AlN/sapphire), 0.9 mW (ELO AlN/sapphire), and 1.1 mW (HTA ELO AlN/sapphire), respectively. Furthermore, Monte Carlo ray-tracing simulations showed a 15% increase in light-extraction efficiency due to the voids formed in the ELO process. These results demonstrate that HTA ELO AlN/sapphire templates provide a viable approach to increase the efficiency of UV-LEDs, improving both the internal quantum efficiency and the light-extraction efficiency.

No abstract

No abstract