High crystalline quality coaxial GaInN/GaN multiple quantum shells (MQSs) grown on dislocation-free nanowires are highly in demand for efficient white-/micro-light-emitting diodes (LEDs). Here, we propose an effective approach to improve the MQS quality during the selective growth by metal–organic chemical vapor deposition. By increasing the growth temperature of GaN barriers, the cathodoluminescent intensity yielded enhancements of 0.7 and 3.9 times in the samples with GaN and AlGaN spacers, respectively. Using an AlGaN spacer before increasing the barrier temperature, the decomposition of GaInN quantum wells was suppressed on all planes, resulting in a high internal quantum efficiency up to 69%. As revealed by scanning transmission electron microscopy (STEM) characterization, the high barrier growth temperature allowed to achieve a clear interface between GaInN quantum wells and GaN quantum barriers on the c-, r-, and m-planes of the nanowires. Moreover, the correlation between the In incorporation and structure features in MQS was quantitatively assessed based on the STEM energy-dispersive X-ray spectroscopy mapping and line-scan profiles of In and Al fractions. Ultimately, it was demonstrated that the unintentional In incorporation in GaN barriers was induced by the evaporation of predeposited In-rich particles during low-temperature growth of GaInN wells. Such residual In contamination was sufficiently inhibited by inserting low Al fraction (∼6%) AlGaN spacers after each GaInN well. During the growth of AlGaN spacers, AlN polycrystalline particles were deposited on the surrounding dummy substrate, which suppressed the evaporation of the predeposited In-rich particles. Thus, the presence of AlGaN spacers certainly improved the uniformity of In fraction through five GaInN quantum wells and reduced the diffusion of point defects from n-core to MQS active structures. The superior coaxial GaInN/GaN MQS structures with the AlGaN spacer are supposed to improve the emission efficiency in white-/micro-LEDs.

Broadened emission was demonstrated in coaxial GaInN/GaN multiple quantum shell (MQS) nanowires that were monolithically grown by metalorganic chemical vapor deposition. The non-polar GaInN/GaN structures were coaxially grown on n-core nanowires with combinations of three different diameters and pitches. To broaden the emission band in these three nanowire patterns, we varied the triethylgallium (TEG) flow rate and the growth temperature of the quantum barriers and wells, and investigated their effects on the In incorporation rate during MQS growth. At higher TEG flow rates, the growth rate of MQS and the In incorporation rate were promoted, resulting in slightly higher cathodoluminescence (CL) intensity. An enhancement up to 2–3 times of CL intensity was observed by escalating the growth temperature of the quantum barriers to 800 °C. Furthermore, decreasing the growth temperature of the quantum wells redshifted the peak wavelength without reducing the MQS quality. Under the modified growth sequence, monolithically grown nanowires with a broaden emission was achieved. Moreover, it verified that reducing the filling factor (pitch) can further promote the In incorporation probability on the nanowires. Compared with the conventional film-based quantum well LEDs, the demonstrated monolithic coaxial GaInN/GaN nanowires are promising candidates for phosphor-free white and micro light-emitting diodes (LEDs).

No abstract

Multi-color emission was identified from coaxial GaInN/GaN multiple-quantum-shells (MQS) nanowire-based light-emitting diodes (LEDs). In this study, the MQS nanowire samples for LED processes were selectively grown on patterned commercial GaN/sapphire...

No abstract