The demonstration that Nanocrystalline Diamond (NCD) can retain the superior Young's modulus (1,100 GPa) of single crystal diamond twinned with its ability to be grown at low temperatures (<450 {\deg}C) has driven a revival into the growth and applications of NCD thin films. However, owing to the competitive growth of crystals the resulting film has a roughness that evolves with film thickness, preventing NCD films from reaching their full potential in devices where a smooth film is required. To reduce this roughness, films have been polished using Chemical Mechanical Polishing (CMP). A Logitech Tribo CMP tool equipped with a polyurethane/polyester polishing cloth and an alkaline colloidal silica polishing fluid has been used to polish NCD films. The resulting films have been characterised with Atomic Force Microscopy, Scanning Electron Microscopy and X-ray Photoelectron Spectroscopy. Root mean square roughness values have been reduced from 18.3 nm to 1.7 nm over 25 {\mu}m$^2$, with roughness values as low as 0.42 nm over ~ 0.25 {\mu}m$^2$. A polishing mechanism of wet oxidation of the surface, attachment of silica particles and subsequent shearing away of carbon has also been proposed.Comment: 6 pages, 6 figure

In this paper, the origin of positive zeta potential exhibited by nanodiamond particles is explained. Positive zeta potentials in nano-structured carbons can be explained by the presence of graphitic planes at the surface, which leave oxygen-free Lewis sites and so promotes the suppression of acidic functional groups. Electron Microscopy and Raman Spectroscopy have been used to show that positive zeta potential of nanodiamond is only exhibited in the presence of sp carbon at the surface.

Optical trapping at high vacuum of a nanodiamond containing a nitrogen vacancy centre would provide a test bed for several new phenomena in fundamental physics. However, the nanodiamonds used so far have absorbed too much of the trapping light, heating them to destruction (above 800 K) except at pressures above ∼10 mbar where air molecules dissipate the excess heat. Here we show that milling diamond of 1000 times greater purity creates nanodiamonds that do not heat up even when the optical intensity is raised above 700 GW m −2 below 5 mbar of pressure.

Diamond is an electrical insulator in its natural form. However, when doped with boron above a critical level (∼0.25 atom %) it can be rendered superconducting at low temperatures with high critical fields. Here we present the realization of a micrometer-scale superconducting quantum interference device (μ-SQUID) made from nanocrystalline boron-doped diamond (BDD) films. Our results demonstrate that μ-SQUIDs made from superconducting diamond can be operated in magnetic fields as large as 4 T independent of the field direction. This is a decisive step toward the detection of quantum motion in a diamond-based nanomechanical oscillator.