Two Cu-Zn-Al alloys with variable content of Zn (25 and 30 wt%) and constant Al content (4 wt%) prepared by induction melting of pure metals and hot rolled into strips of 0.5 mm thickness were thermally processed by using three different heat treatments: direct quenching, step-quenching and upquenching with boiling water and room temperature water as the quenchants. The effects of composition and different methods of heat treatment on the microstructure and transformation temperatures of the investigated Cu-Zn-Al alloys were investigated using SEM-EDS and DSC techniques.

No abstract

Four Cu-rich alloys from the ternary Cu-Al-Mn system were prepared in the electric-arc furnace and casted in cylindrical moulds with dimensions: =8 mm and length 12 mm. Microstructural investigations of the prepared samples were performed by using optical microscopy (OM) and scanning electron microscopy, equipped by energy dispersive spectroscopy (SEM-EDS). Assignation of crystalline phases was confirmed by XRD analysis. Phase transition temperatures were determined using simultaneous thermal analyzer STA DSC/TG. Phase equilibria calculation of the ternary Cu-Al-Mn system was performed using optimized thermodynamic parameters from literature. Microstructure and phase transitions of the prepared as-cast alloys were investigated and experimental results were compared with the results of thermodynamic calculations.

No abstract