Components subject to rolling contact fatigue, such as gears and rolling bearings, are among the fundamental machine elements in mechanical and vehicle engineering. Rolling bearings are generally not designed to be fatigue-resistant, as the necessary oversizing is not technically and economically marketable. In order to improve the load-bearing capacity, resource efficiency and application possibilities of rolling bearings and other possible multi-material solid components, a new process chain was developed at Leibniz University Hannover as a part of the Collaborative Research Centre 1153 “Tailored Forming”. Semi-finished products, already joined before the forming process, are used here to allow a further optimisation of joint quality by forming and finishing. In this paper, a plasma-powder-deposition welding process is presented, which enables precise material deposition and control of the welding depth. For this study, bearing washers (serving as rolling bearing raceways) of a cylindrical roller thrust bearing, similar to type 81212 with a multi-layer structure, were manufactured. A previously non-weldable high-performance material, steel AISI 5140, was used as the cladding layer. Depending on the degree of forming, grain-refinement within the welded material was achieved by thermo-mechanical treatment of the joining zone during the forming process. This grain-refinements lead to an improvement of the mechanical properties and thus, to a higher lifetime for washers of an axial cylindrical roller bearing, which were examined as an exemplary component on a fatigue test bench. To evaluate the bearing washers, the results of the bearing tests were compared with industrial bearings and deposition welded axial-bearing washers without subsequent forming. In addition, the bearing washers were analysed micro-tribologically and by scanning acoustic microscopy both after welding and after the forming process. Nano-scratch tests were carried out on the bearing washers to analyse the layer properties. Together with the results of additional microscopic images of the surface and cross-sections, the causes of failure due to fatigue and wear were identified.

To enhance tribological contacts under cyclic load, high performance materials are required. Utilizing the same high-strength material for the whole machine element is not resource-efficient. In order to manufacture machine elements with extended functionality and specific properties, a combination of different materials can be used in a single component for a more efficient material utilization. By combining different joining techniques with subsequent forming, multi-material or tailored components can be manufactured. To reduce material costs and energy consumption during the component service life, a less expensive lightweight material should be used for regions remote from the highly stressed zones. The scope is not only to obtain the desired shape and dimensions for the finishing process, but also to improve properties like the bond strength between different materials and the microscopic structure of the material. The multi-material approach can be applied to all components requiring different properties in separate component regions such as shafts, bearings or bushes. The current study exemplarily presents the process route for the production of an axial bearing washer by means of tailored forming technology. The bearing washers were chosen to fit axial roller bearings (type 81212). The manufacturing process starts with the laser wire cladding of a hard facing made of martensitic chromium silicon steel (1.4718) on a base substrate of S235 (1.0038) steel. Subsequently, the bearing washers are forged. After finishing, the surfaces of the bearing washers were tested in thrust bearings on an FE-8 test rig. The operational test of the bearings consists in a run-in phase at 250 rpm. A bearing failure is determined by a condition monitoring system. Before and after this, the bearings were inspected by optical and ultrasonic microscopy in order to examine whether the bond of the coat is resistant against rolling contact fatigue. The feasibility of the approach could be proven by endurance test. The joining zone was able to withstand the rolling contact stresses and the bearing failed due to material-induced fatigue with high cycle stability.

Hybrid cylindrical roller thrust bearing washers of type 81212 were manufactured by tailored forming. An AISI 1022M base material, featuring a sufficient strength for structural loads, was cladded with the bearing steel AISI 52100 by plasma transferred arc welding (PTA). Though AISI 52100 is generally regarded as non-weldable, it could be applied as a cladding material by adjusting PTA parameters. The cladded parts were investigated after each individual process step and subsequently tested under rolling contact load. Welding defects that could not be completely eliminated by the subsequent hot forming were characterized by means of scanning acoustic microscopy and micrographs. Below the surface, pores with a typical size of ten µm were found to a depth of about 0.45 mm. In the material transition zone and between individual weld seams, larger voids were observed. Grinding of the surface after heat treatment caused compressive residual stresses near the surface with a relatively small depth. Fatigue tests were carried out on an FE8 test rig. Eighty-two percent of the calculated rating life for conventional bearings was achieved. A high failure slope of the Weibull regression was determined. A relationship between the weld defects and the fatigue behavior is likely.

The production process significantly influences the surface properties of rolling element bearings raceways. Deep rolling can induce a depth dependent residual stress state. Previous numerical and experimental studies have shown that rolling bearings fatigue life can be positively influenced by high compressive residual stress to a depth of around 300 µm from the surface. By extending the components life, the resource efficiency of machine components can be increased. In order to determine the influence of the residual stress state in bearing fatigue life, a calculation method was developed for predicting the bearing fatigue life. This method was validated for hard-turning and subsequent deep rolling by experiments on a test rig in four-bearing configuration under radial load. An increase of the L 10 bearing life by a factor of 2.5 has been achieved by inducing residual stresses on the bearing's inner ring. Due to similar process control, the manufacturing steps turning and deep rolling were combined. Bearings were manufactured combining the processes hard-turning and deep rolling (called turn-rolling). The heat from the hard machining has an effect on the residual stresses in the bearing subsurface, thus further altering the magnitude and maximum depth of the residual stress influencing the microstructure. With these bearings, the additional fatigue life was determined experimentally and compared to the results of the bearings produced by hard-turning and subsequent deep rolling. It could be shown, that the process of hard turning and subsequent deep rolling has highest potential to achieve improved bearing fatigue life. These findings were transferred to a "Tailored Forming" shaft with integrated raceway in a second step. In this case, a shaft made of mild steel is combined with a cladding layer of high strength bearing steel to be used as a bearing raceway.

By combining different materials, for example, high-strength steel and unalloyed structural steel, hybrid components with specifically adapted properties to a certain application can be realized. The mechanical processing, required for production, influences the subsurface properties, which have a deep impact on the lifespan of solid components. However, the influence of machining-induced subsurface properties on the operating behavior of hybrid components with a material transition in axial direction has not been investigated. Therefore, friction-welded hybrid shafts were machined with different process parameters for hard-turning and subsequent deep rolling. After machining, subsurface properties such as residual stresses, microstructures, and hardness of the machined components were analyzed. Significant influencing parameters on surface and subsurface properties identified in analogy experiments are the cutting-edge microgeometry, S¯, and the feed, f, during turning. The deep-rolling overlap, u, hardly changes the residual stress depth profile, but it influences the surface roughness strongly. Experimental tests to determine fatigue life under combined rolling and rotating bending stress were carried out. Residual stresses of up to −1000 MPa, at a depth of 200 µm, increased the durability regarding rolling-contact fatigue by 22%, compared to the hard-turned samples. The material transition was not critical for failure.