The study deals with chemical and flame retardant (FR) treatment of flax fabric. Sheets of flax fabric were subjected to chemical treatments using NaOH and silane coupling agents. A phosphate‐based flame retardant (DAP) was also applied to improve the flammability of the fabric. The effects of the chemical treatments and FR treatments on flax fabric were investigated using Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and vertical flame resistance test. Aging studies were carried out by exposing the samples in an environmental chamber at specified conditions for two weeks. The mechanical properties of the fabric, before and after environmental aging, were investigated. Flammability of flax fabric was improved after FR treatment. Thermal studies revealed a shift of decomposition temperature to lower temperatures and an increase in char residue after FR treatment. Despite treatment of the fabric with NaOH and silane, the tensile strength of FR‐treated flax fabric declined by more than 90% after aging for two weeks at 90 °C and 50% RH. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 44175.

SummaryIn this study, flax composites were prepared from flax fabric and phenolic resin. Chemical treatments were imparted to the fabric to improve adhesion between the fabric and the phenolic matrix. Diammonium phosphate was applied to improve the flammability of the composites.The thermal and flammability properties of the untreated, chemically treated, and flame retardant (FR) treated flax fabric reinforced phenolic composites were studied. Ageing studies were carried out by subjecting the composites to varying conditions of temperature and humidity in an environmental chamber for 2 weeks. FR treatment of flax fabric was shown to be very effective in improving flame retardancy of the composites due to decreased peak heat release rate (PHRR) and smoke production rate (SPR). Thermogravimetric analysis (TGA) of composites showed that after FR treatment, the decomposition temperatures shifted to lower temperatures. Ageing studies revealed that the mechanical properties of untreated, chemically treated and FR treated composites decreased with an increase in ageing temperature.

No abstract