We report blue-purple pn-junction light-emitting diodes (LEDs) with a-plane GaN–InGaN multiple quantum well active region. The LEDs were grown over r-plane sapphire substrates. Our study has shown the low pump intensity photoluminencence and electroluminescence to be dominated by emission from the band-tail states which then saturates rapidly giving rise to band-edge emission.

We report AlGaN deep ultraviolet light-emitting diodes (LEDs) at 250 and 255nm that have short emission wavelengths. For an unpackaged 200×200μm square geometry LED emitting at 255nm, we measured a peak power of 0.57mW at 1000mA of pulsed pump current. For a similar device emitting at 250nm the peak output power of 0.16mW was measured at 300mA of pulsed pump current. Progress is based on the development of high quality AlGaN cladding layers with an Al content up to 72%, which were grown over AlGaN∕AlN superlattice buffer layers on sapphire substrates. These n-Al0.72Ga0.28N layers were doped with Si up to about 1×1018cm−3 and electron mobilities up to 50cm2∕V∙s were estimated. High resolution x-ray diffraction studies gave a narrow (002) rocking curve with full width at half maximum of only 133arcsec.

We report on AlGaN multiple-quantum-well (MQW)-based deep ultraviolet light-emitting diodes over sapphire with peak emission at 278 nm. A new buffer layer growth process was used to reduce the number of defects and hence the nonradiative recombination. The improved material quality and carrier confinement resulted in pulsed powers as high as 3 mW at 278 nm and a significantly reduced deep-level-assisted long-wavelength emission.

No abstract

We report on 269 nm emission deep ultraviolet light-emitting diodes (LEDs) over sapphire. The material quality, device design, and contact processing sequence yielded devices with external quantum efficiencies as high as 0.4% for a pumped pulse current of 200 mA and 0.32% for a dc pump current of 10 mA. For a module of two LEDs connected in series, a record continuous-wave power of 0.85 mW (at 40 mA) and a wall plug efficiency of 0.16% (at 10 mA dc) were measured.