Effective removal of oils, organic solvents and dyes from water is of significant, global importance for environmental and water source protection. Advanced sorbent materials with excellent sorption capacity need to be developed. Here we report porous boron nitride nanosheets with very high specific surface area that exhibit excellent sorption performances for a wide range of oils, solvents and dyes. The nanostructured material absorbs up to 33 times its own weight in oils and organic solvents while repelling water. The saturated boron nitride nanosheets can be readily cleaned for reuse by burning or heating in air because of their strong resistance to oxidation. This easy recyclability further demonstrates the potential of porous boron nitride nanosheets for water purification and treatment.

Manufacturing of aerogels and membranes from hexagonal boron nitride (h-BN) is much more difficult than from graphene or graphene oxides because of the poor dispersibility of h-BN in water, which limits its exfoliation and preparation of colloidal solutions. Here, a simple, one-step mechano-chemical process to exfoliate and functionalize h-BN into highly water-dispersible, few-layer h-BN containing amino groups is presented. The colloidal solutions of few-layer h-BN can have unprecedentedly high concentrations, up to 30 mg ml−1, and are stable for up to several months. They can be used to produce ultralight aerogels with a density of 1.4 mg cm−3, which is ∼1,500 times less than bulk h-BN, and freestanding membranes simply by cryodrying and filtration, respectively. The material shows strong blue light emission under ultraviolet excitation, in both dispersed and dry state.

The discovery of liquid crystalline (LC) phases in dispersions of two-dimensional (2D) materials has enabled the development of macroscopically aligned three-dimensional (3D) macrostructures. Here, we report the first experimental observation of self-assembled LC phases in aqueous Ti 3 C 2 T x MXene inks without using LC additives, binders, or stabilizing agents. We show that the transition concentration from the isotropic to nematic phase is influenced by the aspect ratio of MXene flakes. The formation of the nematic LC phase makes it possible to produce fibers from MXenes using a wet-spinning method. By changing the Ti 3 C 2 T x flake size in the ink formulation, coagulation bath, and spinning parameters, we control the morphology of the MXene fibers. The wet-spun Ti 3 C 2 T x fibers show a high electrical conductivity of ∼7750 S cm −1 , surpassing existing nanomaterial-based fibers. A high volumetric capacitance of ∼1265 F cm −3 makes Ti 3 C 2 T x fibers promising for fiber-shaped supercapacitor devices. We also show that Ti 3 C 2 T x fibers can be used as heaters. Notably, the nematic LC phase can be achieved in other MXenes (Mo 2 Ti 2 C 3 T x and Ti 2 CT x ) and in various organic solvents, suggesting the widespread LC behavior of MXene inks.

A simple, high yield, chemical process is developed to fabricate layered h-BN nanosheets and BCNO nanoparticles with a diameter of ca. 5 nm at 700 °C. The use of the eutectic LiCl/KCl salt melt medium enhances the kinetics of the reaction between sodium borohydride and urea or guanidine as well as the dispersion of the nanoparticles in water. The carbon content can be tuned from 0 to 50 mol % by adjusting the reactant ratio, thus providing precise control of the light emission of the particles in the range 440-528 nm while reaching a quantum yield of 26%. Because of their green synthesis, low toxicity, small size, and stability against aggregation in water, the as-obtained photoluminescent BCNO nanoparticles show promise for diagnostics and optoelectronics.

No abstract