No abstract

In-situ forming hydrogels have gained noticeable attention to encapsulate osteogenic agents and regenerate irregular-shape bone defects. In this study, a novel thermosensitive hydrogel based on blended methylcellulose (MC) with Persian gum (PG) was fabricated and enriched with taxifolin (TAX) loaded halloysite nanotubes (HNTs) to enhance mechanical and biological characteristics of the hydrogel in bone tissue engineering. The injectability, mechanical and rheological tests were performed for different hydrogel formulations containing 0.25-1.5 w/v% PG and 1-7 w/v% HNTs. Also, to evaluate the impact of PG and HNTs on hydrogel behavior, the degradation rate and swelling degree of hydrogels were assessed. The optimized MC/PG/HNTs hydrogel containing 1% PG and 3% HNTs (MC/PG-1/HNTs 3%) was easily injectable and gelled rapidly at physiological temperature, while it had the highest mechanical strength due to the existence of PG and HNTs. In vitro release study of TAX from this system also revealed more sustained release compared to HNTs-TAX nanoparticles. Furthermore, the interaction of cells with hydrogel and osteo-conductivity was studied using osteoblast-like cells (MG-63). Results showed higher cell adhesion, proliferation, and gene expression for MC/PG-1/HNTs-TAX hydrogel compared to MC/PG-1 and MC/PG-1/HNTs 3% possibly due to the synergic effect of HNTs and TAX. In addition, Alizarin Red S staining and alkaline phosphatase measurements indicated that the existence of HNTs-TAX promoted osteogenic differentiation. Eventually, animal studies on the femoral defects indicated improved remedy when using the MC/PG-1/HNTs-TAX hydrogel carrying MG-63 cells.'Al 2 Si 2 O 5 (OH) 4 •nH2O' are safe, biocompatible and cheap aluminosilicate clay, which have been used as a

Oral and maxillofacial tissue defects caused by trauma, tumor reactions, congenital anomalies, ischemic diseases, infectious diseases, surgical resection, and odontogenic cysts present a formidable challenge for reconstruction. Tissue regeneration using functional biomaterials and cell therapy strategies has raised great concerns in the treatment of damaged tissue during the past few decades. However, during biomaterials implantation and cell transplantation, the production of excessive reactive oxygen species (ROS) may hinder tissue repair as it commonly causes severe tissue injuries leading to the cell damage. These products exist in form of oxidant molecules such as hydrogen peroxide, superoxide ions, hydroxyl radicals, and nitrogen oxide. These days, many scientists have focused on the application of ROS-scavenging components in the body during the tissue regeneration process. One of these scavenging components is antioxidants, which are beneficial materials for the treatment of damaged tissues and keeping tissues safe against free radicals. Antioxidants are divided into natural and synthetic sources. In the current review article, different antioxidant sources and their mechanism of action are discussed. The applications of antioxidants in the regeneration of oral and maxillofacial tissues, including hard tissues of cranial, alveolar bone, dental tissue, oral soft tissue (dental pulp, periodontal soft tissue), facial nerve, and cartilage tissues, are also highlighted in the following parts.

In-situ forming hydrogels have gained noticeable attention to encapsulate osteogenic agents and regenerate irregular-shape bone defects. In this study, a novel thermosensitive hydrogel based on blended methylcellulose (MC) with Persian gum (PG) was fabricated and enriched with taxifolin (TAX) loaded halloysite nanotubes (HNTs) to enhance mechanical and biological characteristics of the hydrogel in bone tissue engineering. The injectability, mechanical and rheological tests were performed for different hydrogel formulations containing 0.25-1.5 w/v% PG and 1-7 w/v% HNTs. Also, to evaluate the impact of PG and HNTs on hydrogel behavior, the degradation rate and swelling degree of hydrogels were assessed. The optimized MC/PG/HNTs hydrogel containing 1% PG and 3% HNTs (MC/PG-1/HNTs 3%) was easily injectable and gelled rapidly at physiological temperature, while it had the highest mechanical strength due to the existence of PG and HNTs. In vitro release study of TAX from this system also revealed more sustained release compared to HNTs-TAX nanoparticles. Furthermore, the interaction of cells with hydrogel and osteo-conductivity was studied using osteoblast-like cells (MG-63). Results showed higher cell adhesion, proliferation, and gene expression for MC/PG-1/HNTs-TAX hydrogel compared to MC/PG-1 and MC/PG-1/HNTs 3% possibly due to the synergic effect of HNTs and TAX. In addition, Alizarin Red S staining and alkaline phosphatase measurements indicated that the existence of HNTs-TAX promoted osteogenic differentiation. Eventually, animal studies on the femoral defects indicated improved remedy when using the MC/PG-1/HNTs-TAX hydrogel carrying MG-63 cells.