In this study, in-plane and out-plane compression tests of aluminum foam and honeycomb sandwich composites were carried out. Through these tests, the relationships of load-displacements were analyzed and the compression characteristics were compared with each other. The specimens were compressed with the speed of 1mm/min by using the universal testing machine. Experimental procedures were taken with photograph by the camera and load cell data were stored into computer. Test results showed that buckling was occurred at the aluminum foam core and honeycomb core according to the increase of load. In the in-plane compression test, the maximum load of aluminum foam specimen was similar with that of honeycomb sandwich. The property of honeycomb was better than that of the foam in consideration of specific gravity. In the out-plane compression test, compression maximum load of aluminum honeycomb sandwich composite was higher than that of aluminum foam sandwich composite.

No abstract

Among the various parts of automobile, automotive seat is the most fundamental item that ride comfort can be evaluated as the direct contact part with human body. Automotive seat must have the sufficient rigidity and strength at the same time with ride comfort. In this study, cushion frame and back frame at car seat are modelled with 3D. There are structural simulation analyses about 3 kinds of tests on torsion strength, vertical load strength and back frame strength. In the analysis result, the initial total deformation and the permanent total deformation has the maximum values of 5.4821 mm and 0.02539mm respectively at the torsion strength test of cushion frame. Total deformations at front and rear end parts of cushion frame become the values of 2.1159mm and 0.0606mm respectively at the test of vertical load strength of cushion frame. In case of more than this load, the maximum value of total deformation also becomes 3.1739mm. The maximum value of total deformation becomes 0.18634mm at 3 kinds of the strength tests on back frame. By the study result of no excessive deformation and no fracture cushion frame and back frame at automotive seat, the sufficient rigidity and strength to guarantee the safety of passenger can be verified.

Therefore, to establish optimal condition and composition with magnesium chloride emulsion as coagulant, this study compared its properties by the usage of 60%(w/w) magnesium chloride solution, lastly measured the characteristics of soybean curd coagulation, coagulation time, state of texture, and water separation ratio with using emulsion as coagulant. After all the experiments, when manufacturing magnesium chloride emulsion with using 70% of quantity of 60%(w/w) magnesium chloride solution, it had the best result as coagulant according to the state of texture and the water separation ratio of soybean curd.