Mechanical properties of recycled kenaf/polyethylene terephthalate (PET) fiber reinforced polyoxymethylene (POM) hybrid composite

Abstract

Environmental concerns have attracted researchers to study the recycling of composite materials and thermoplastics due to the desire not to waste materials and reduce disposal of scraps that may eventually pollute the environment. The main objective of this article is to study the effect of recycling on the mechanical properties of kenaf fiber/PET reinforced POM hybrid composite. The virgin hybrid composite was produced by compression molding and later subjected to mechanical testing. The scraps obtained after the mechanical testing were shredded, granulated and subjected to compression molding to produce samples for mechanical testing. Tensile strength of 27 MPa was obtained and (after second recycling process) which is lower compared to 73.8 MPa obtained for the virgin hybrid composite. There was a significant increase in flexural modulus (4.7 GPa) compared to the virgin hybrid composite. The impact strength dropped to 4.3 J cm−1 as against 10.5 J cm−1 for the virgin hybrid composite. The results of thermal degradation showed about 80% weight loss for kenaf fiber between 300 and 350°C. The weight loss may be due to the degradation of cellulose and hemicellulose content of the fiber. The percentage water absorption of the recycled composite dropped by about 80% compared to the virgin hybrid composite. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014, 131, 39831.

Development of Sustainable and Cost-Competitive Injection-Molded Pieces of Partially Bio-Based Polyethylene Terephthalate through the Valorization of Cotton Textile Waste

“…Indeed, lignin starts its degradation at about 250 °C and its corresponding degradation process is prolonged up to temperatures around 450 °C [74]. Moreover, cellulose degrades in the 300–400 °C range and full decomposition takes place from 450 °C [22,75,76]. To ascertain the thermal stability of the neat bio-PET piece and the bio-PET/RCF composite pieces, thermogravimetric analysis (TGA) was carried out up to 700 °C and the resultant plots are gathered in Figure 4.…”

Effect of Environmental Degradation on Mechanical Properties of Kenaf/Polyethylene Terephthalate Fiber Reinforced Polyoxymethylene Hybrid Composite

“…This may further reduce its crystallinity and elasticity due to long time exposure in the weathering chamber. Previous study on recycling of the hybrid composite also explained why a reduction in molecular weight and thermal degradation affected the mechanical properties of the hybrid composite [22]. The degradation of the kenaf fiber may be due to the effect of high humidity and UV on cellulose, hemicellulose, and lignin content of the fiber during exposure in the accelerated weathering chamber.…”

Improving the mechanical properties of p‐aramid fabrics and composites by developing ZnO nanostructures

“…Epoxy resin (Araldite LY556) was used in combination with 10% of Araldite HY932 hardener. Resin was applied on single layer of Kevlar fabric by hand lay‐up technique . Composite samples were prepared in compression molding machine at 120°C temperature with applied force of 1 ton for 20 minutes.…”