PEMBUATAN SELULOSA ASETAT DARI PULP KENAF (Hibiscus cannabinus)

Widyaningsih, Senny; Radiman, Cynthia Linaya

doi:10.20884/1.jm.2007.2.1.181

Cited by 6 publications

(5 citation statements)

References 0 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Glacial acetic acid serves as a pretreatment agent that aims to inflate the cellulose fibers to be more open so that it can accelerate the acetylation reaction with acetic anhydrous and increase cellulose reactivity and to reduce the degree of polymerization to a level suitable for acetylation. Sulfuric acid functions as a catalyst and anhydrous acetic acid functions as an acetyl donor (Widyaningsih and Radiman, 2007).…”

Section: Preliminarymentioning

confidence: 99%

Synthesis of Acetate Cellulosa From the Palm Oil Empty Floor Through the Reaction of Activation

Mauliana¹,

Kurniasih²,

Syafruddin³

2019

J.Scien.Techno.Reaction

View full text Add to dashboard Cite

Acetate cellulose is cellulose whose hydroxyl group is replaced by an acetyl group. Celluloseacetate has a high enough attractiveness because it is biodegradable so it is environmentally friendly. The purpose of this study is to increase the acetyl content of cellulose acetate by theacetylation reaction. This study uses 25 grams of empty fruit bunches to get cellulose, the delignification process is carried out for 30 minutes with NaOH solution, and the bleachingprocess for 1.5 hours with H2O2 solution. Next, as much as 5 grams of cellulose was carriedout by the acetylation process by adding glacial CH3COOH solution, anhydrous CH3COOHsolution with a ratio of 1:10, 1: 12.5 and 1:15 (w / v) and H2SO4 as a catalyst, withtemperature variations of 40oC, 55oC and 70oC. Next, an acetyl concentration was analyzedby titration, and substitution degree analysis was carried out. The best results obtained fromthe two analyzes will be carried out the Fourier Transform Infrared (FTIR) test and theScanning Electron Microscope (SEM) test. Acetyl content obtained was 8,152 - 24,58% andthe degree of substitution obtained was 0,3 - 1,2%.

show abstract

Section: Preliminarymentioning

confidence: 99%

Synthesis of Acetate Cellulosa From the Palm Oil Empty Floor Through the Reaction of Activation

Mauliana¹,

Kurniasih²,

Syafruddin³

2019

J.Scien.Techno.Reaction

View full text Add to dashboard Cite

show abstract

“…Selulosa asetat dapat disintesis dari bahan alam. Selulosa asetat dapat disintesis dari serat daun nanas, bahan baku koran [2] , limbah kapas [3] , jerami [4] , dan pulp kenaf [5] . Salah satu sumber selulosa yang dapat dimodifikasi menjadi selulosa asetat adalah sabut pinang [6] .…”

Section: Pendahuluanunclassified

“…Penentuan nilai viskositas intrinsik ini dilakukan dengan 2 persamaan, yaitu melakukan plot data menggunakan persamaan Huggins (persamaan 3) dan persamaan (5). Hasil plot data disajikan pada Gambar 1 dan 2 dan Tabel 1 sebagai berikut : Persamaan (3) merupakan Persamaan Huggins yang memperhitungkan pengaruh interaksi antara pelarut dan zat terlarut.…”

Section: 1penentuan Nilai Viskositas Intrinsikunclassified

Kinetika Degradasi Selulosa Asetat Dari Sabut Pinang

Syahbanu

Anugraini

Melati

2018

IJoPAC

View full text Add to dashboard Cite

Cellulose Acetate is a material with wide range in applications. Cellulose acetate may obtain from natural resources, such as areca fiber. Polymers should have uniform molecular weight for the applications and could be modify by ultrasonic waves. Ultrasonic treatment on polymer entangled with polymer degradation. In this research, degradation kinetics of cellulose acetate in acetone had been studied. Analysis was performed by determination of intrinsic viscosity in polymer solution system. Intrinsic viscosity was successfully obtained by fitting data using Huggins equation, indicate molecular interaction in polymer solution should not be neglected. Increasing in sonication time reducing the intrinsic viscosities as well as molecular size in solutions. Degradation rate constant and reaction order were obtained 5,975x10 -3 (g.mL -1 ) 0,1 .min -1 and 1,0616, respectively. Kinetics model was successful to determine the degradation rates of cellulose acetate on acetone by correlation coefficient (R 2 ) at 0,966. © 2018 IJoPAC. All rights reserved PendahuluanSelulosa asetat (SA) merupakan ester organik selulosa yang berupa padatan putih, tidak berbau dan tidak berasa serta merupakan ester yang paling penting yang berasal dari asam organik [1] . Selulosa asetat dapat disintesis dari bahan alam. Selulosa asetat dapat disintesis dari serat daun nanas, bahan baku koran [2] , limbah kapas [3] , jerami [4] , dan pulp kenaf [5] . Salah satu sumber selulosa yang dapat dimodifikasi menjadi selulosa asetat adalah sabut pinang [6] . Selulosa asetat yang dihasilkan tergolong selulosa diasetat dengan nilai derajat subtitusi berkisar pada 2,8-2,9. Selulosa asetat memiliki nilai komersil yang baik dan telah diaplikasikan secara luas sebagai filter, plastik ramah lingkungan, dan dalam industri kertas dan tekstil.Terkait dengan aplikasinya, diperlukan material dengan distribusi massa molekul yang sempit, sehingga ukurannya lebih seragam. Modifikasi material ini dapat melibatkan proses degradasi polimer. Beberapa teknik telah diterapkan dalam modifikasi material, salah satunya dengan teknik sonikasi. Sonikasi termasuk metode yang cepat dan mudah, tidak membutuhkan banyak penambahan bahan kimia, tidak mengakibatkan perubahan yang signifikan pada struktur kimia partikel dan senyawa bahan baku yang digunakan [7] .Penggunaan sonikasi dapat menyebabkan perubahan massa molekul rata-rata viskositas (Mv) dengan adanya reduksi viskositas akibat pemberian gelombang ultrasonik [8] . Beberapa penelitian sebelumnya menyebutkan bahwa terjadinya reduksi viskositas pada larutan polimer yang diberi gelombang ultrasonik. Hal ini dinyatakan bahwa hubungan larutan polimer yang

show abstract

“…(2012) yang menjelaskan bahwa kemunculan puncak pada 8 o menunjukkan adanya susunan kristal tidak beraturan (disorder) dari selulosa terasetilasi. Gambar 7 lebih jauh menjelaskan bahwa tidak terdapat puncak yang tajam pada jumlah katalis 3% yang menunjukkan bahwa selulosa terasetilasi bersifat lebih amorf karena proses asetilasi merusak susunan kristalin pada selulosa seperti dijelaskan oleh Widyaningsih dan Radiman (2007).…”

Section: X-ray Diffraction (Xrd)unclassified

“…Modifikasi kimia selulosa dari MFC dengan proses asetilasi telah dilakukan dengan kondisi operasi di bawah suhu ruang 0-25 o C dan menghasilkan selulosa terasetilasi dengan bentuk gel dan serbuk (Widyaningsih dan Radiman, 2007;Yang dkk., 2008;Gaol dkk., 2013). Sementara itu Abdulkhani (2014) menggunakan suhu 100 o C untuk asetilasi nano MFC.…”

unclassified