No abstract

Many types of porous particles containing inorganic and organic substances, such as carbon, metals, metal oxides, inorganic−organic hybrids, and polymers, have been developed. However, natural polymer-derived particles are relatively rare. To our knowledge, this report describes the first synthetic method for obtaining meso-/macroporous particles made from pectin, which is a natural polymer with a wide range of biological activities suitable for active substance support applications. These porous particles were prepared using a template-assisted spray-drying method, followed by a chemical etching process. An organic template [i.e., poly(methyl methacrylate) (PMMA)] or an inorganic template [i.e., calcium carbonate (CaCO 3 )] was used to evaluate the resulting formation of macroporous structures in the pectin particles. Furthermore, the concentration of the templates in the precursor solution was varied to better understand the mechanism of porous pectin particle formation. The results showed that the final porous particles maintained the characteristic properties of pectin. The differences between the two templates resulted in two distinct types of porous particles that differed in their particle morphologies (i.e., spherical or wrinkled), particle sizes (ranging from 3 to 8 μm), pore sizes (ranging from 80 to 350 nm), and pore volume (ranging from 0.024 to 1.40 cm 3 g −1 ). Especially, the porous pectin particles using the CaCO 3 template have a significantly high specific surface area of 171.2 m 2 g −1 , which is 114 times higher than that of nonporous pectin particles. These data demonstrated the potential for using PMMA and CaCO 3 templates to control and design desired porous materials.

No abstract

A green synthetic strategy to design biomassderived porous carbon electrode materials with precisely tailored structure and morphology has always been a challenging goal because these materials can fulfill the demands of next-generation supercapacitors and other electrochemical devices. Potassium hydroxide (KOH) is extensively utilized as an activator since it can produce porous carbon with high specific surface area and well-developed porous channels. The exploitation of sodium hydroxide (NaOH) as an activating agent is less referenced in the literature, although it offers some advantages over KOH in terms of low cost, less corrosiveness, and simple handling procedure, all of which are appealing particularly from an industrial viewpoint. The motivation for this present study is to fabricate porous carbon spheres in a sustainable manner via a spray drying approach followed by a carbonization process, using Kraft lignin as the carbon precursor and NaOH as an alternative activation agent instead of the high-cost and high-corrosive KOH for the first time. The structure of carbon particles can be accurately transitioned from a compact to hollow structure, and the surface textural properties can be easily tuned by altering the NaOH concentration. The obtained porous carbon spheres were applied as highly packed thin film electrode materials for supercapacitor devices. The specific capacitance value of porous carbon spheres with a highly compact structure (high packing density) is 66.5 F g −1 , which is higher than that of commercial activated carbon and other biomassderived carbon. This work provides a green processing for producing low-cost and environment-friendly porous carbon spheres from abundant Kraft lignin and important insight for selecting NaOH as an activator to tailor the morphology and structure, which represents an economical and sustainable approach for energy storage devices.

No abstract