Catalytic pyrolysis experiments have been carried out on Brunei Rice Husk (BRH) to obtain bio-oil using a fixed-bed pyrolysis rig. ZSM-5, Al-MCM-41, Al-MSU-F and Brunei rice husk ash (BRHA) were used as the catalysts for the catalytic pyrolysis experiments and comparison was done to analyse the changes in the bio-oil properties and yield. Properties of the liquid catalytic and non-catalytic bio-oil were analysed in terms of water content, pH, acid number, viscosity, density and calorific value. The bio-oil chemical composition shows that ZSM-5 increases the production of aromatic hydrocarbons and light phenols, whilst Al-MCM-41 reduces the acetic acid production. The catalytic runs increased the calorific value and water content in the bio-oil, whilst viscosity, density and acid number is decreased.

Without pure water, it is impossible to survive for any living beings. The ratio of freshwater on our planet is very poor and the demand is increasing with time for the growing population. Furthermore, water is being contaminated by industrial and agricultural activities, pharmaceuticals, technocratic civilization, pesticides, garments, global changes etc. In addition to this, environmental pollution and global warming are swelling due to the greenhouse and harmful gases generated from the dumping and burning of fossil fuel. Addressing these problems, it is necessary to find out the cost-effective and environmental friendly processes to purify the contaminated water and air. Activated carbons (ACs) are one of the best solutions for removing the pollutants from aqueous and atmosphere as it is the carbonaceous materials with a high degree of porosity, well-developed surface area, and distinguished functional groups which are required for elimination of contaminants. The preparations of activated carbon are easy and safe processes, mainly from the pyrolysis or gasification of biomass with heat and/or chemicals. The recycling and regeneration of activated carbon after use are also essential for resource maintenance and environmental safety. Thus, AC can protect the ecosystem in a double direction by purifying the water and air from the pollutants.

No abstract

No abstract

Pennisetum purpureum is one of the most invasive perennial grasses of the Poaceae family, which are abundant in southeast Asia including Brunei Darussalam. The pyrolysis process at a slow heating rate proved to be highly promising for biochar production. The production and characterization of different Pennisetum purpureum biochars have been investigated at the pyrolysis temperatures of 400 °C, 500 °C and 600 °C with a heating and nitrogen flow rate of 5 °C/min and 0.5 L/min, respectively. The observed higher heating values were 22.18 MJ/kg, 23.02 MJ/kg, 23.75 MJ/kg, and the alkaline pH were 9.10, 9.86, 10.17 for the biochar at 400 °C, 500 °C, 600 °C temperatures, respectively. The water holding capacity was one hundred percent for all biochars and continued to increase for higher pyrolysis temperature. SEM images show that the porosity of the biochars has been enhanced with increased temperatures due to the rearrangement of crystallinity and aromaticity. On the other hand, the yields of biochar have been decreased from 35.13% to 23.02% for the increase of pyrolysis temperature from 400 °C to 600 °C. Energy dispersive X-ray analysis shows that the O/C atomic ratios were 0.15, 0.08 and 0.06 for the biochar of 400, 500 and 600 °C which validates the improvement in heating values. FT-IR analysis revealed that the available functional groups in the biochars were CO , C=C, and C-H. Thermogravimetric analysis (TGA) under pyrolysis condition showed residue of 46.56%, 51.13% and 55.67% from the biochar at 400, 500, and 600 °C, respectively. The derivative thermogravimetry (DTG) graph indicates that the degradation rate is higher for 400 °C biochar than the 600 °C biochar.