The use of AP between alloy metal surfaces and resin cements did not increase the bond strength for most cementing systems evaluated.

Introduction:Disinfection of dentin surfaces is desirable so long as it does not interfere with subsequent bonding of adhesive resins.Objective:To test the null hypothesis that bond strengths to dentin are not affected by previous application of an iodine disinfecting solution.Materials and Methods:Twenty-four extracted non-carious molars were selected. Occlusal enamel was removed producing a flat dentin substrate. Test teeth were all treated with 2% Iodine disclosing/disinfecting solution (I2DDS) for 20 sec and rinsed for 20 sec followed by the application of self- or total- etching bonding systems, generating five adhesive groups (n=3): Single Bond;; Prime & Bond NT; Clearfil SE Bond; Opti-Bond Plus. The control groups (n=3 per adhesive) had no disclosing/disinfectant application prior to adhesive application. A 4-mm thick resin restoration was built up on each tooth for microtensile testing. Statistical analyses between experimental and control groups were performed by student's t-test (α = 0.05).Results:In general, experimental groups (previously treated with I2DDS) showed significantly lower bond strength values when compared with their respective controls (p<0.05), except for group Prime &Bond I2 that did not significantly differ from its control (p>0.05).Conclusion:Acetone-base adhesive systems seem not to be affected by the application of I2DDS prior to etching and bonding procedures.

This study evaluated the antifungal potential of low-temperature plasma (LTP) on a 72-hour Candida albicans biofilm. A growth inhibition zone test was conducted with agar plates inoculated with C. albicans and submitted to LTP and argon application at 3 and 10 mm for 10, 30, 60, 90, and 120 seconds. The groups for biofilm assays were 60 seconds of LTP application with a tip-to-sample distance of 3 mm (LTP-3) and 10 mm (LTP-10); -application of only argon gas for 60 seconds with a tip-to-sample distance of 3 mm (Ar-3) and 10 mm (Ar-10); and no treatment. The C. albicans biofilm was grown on saliva-coated discs. The medium was replaced every 24 hours. Confocal laser scanning microscopy revealed the proportion of live and dead cells, and variable pressure scanning electron microscopy (VPSEM) showed biofilm/cell structure. No inhibition zone was observed for control and either Ar groups. For the LTP groups, a progressively increasing of inhibition zone diameter was observed for different treatment durations. The LTP-3 and LTP-10 groups presented higher proportions of dead cells compared with the Ar-3 and Ar-10 groups. VPSEM revealed cell perforations in the LTP-3 and LTP-10 groups. A short period of LTP exposure demonstrated an antifungal effect on C. albicans biofilm.

No abstract

Aim: There is little information considering the framework association between cast clasps and attachments. The aim of this study was to evaluate the retention strength of frameworks match circumferential clasps and extra resilient attachment cast in three different alloys (cobalt-chromium, nickel-chromium titanium and commercially pure titanium), using two undercut (0.25 and 0.75 mm) and considering different period of time (0, 1/2, 1, 2, 3, 4 and 5 years). Methods:Using two metallic matrices, representing a partially edentulous mandibular right hemiarch with the first molar crown, canine root and without premolars, 60 frameworks were fabricated. Three groups (n = 20) of each metal were cast and each group was divided into two subgroups (n = 10), corresponding the molar undercut of 0.25 mm and 0.75 mm. The nylon male was positioned at the matrix and attached to the acrylic resin of the prosthetic base. The samples were subjected to an insertion and removal test under artificial saliva environment. Results:The data were analyzed and compared with ANOVAs and Tukey's test at 95% of probability. The groups cast in cobaltchromium and nickel-chromium-titanium had the highest mean retention strength (5.58 N and 6.36 N respectively) without significant difference between them, but statistically different from the group cast in commercially pure titanium, which had the lowest mean retention strength in all the periods (3.46 N). The association frameworks using nickel-chromium-titanium and cobalt-chromium could be used with 0.25 mm and 0.75 mm of undercut, but the titanium samples seems to decrease the retention strength, mainly in the 0.75 mm undercut. The circumferential clasps cast in commercially pure titanium used in 0.75 mm undercuts have a potential risk of fractures, especially after the 2nd year of use. Conclusion:This in vitro study showed that the framework association between cast clasp and an extra resilient attachment are suitable to the three metals evaluated, but strongly suggest extra care with commercially pure titanium in undercut of 0.75 mm.Clinical significance: Frameworks fabricated in Cp Ti tend to decrease in retentive strength over time and have a potential risk of fracture in less than 0.75 mm of undercut.