Recent advances have been made in thin-film solar cells using CdTe and CuIn(1-x)Ga(x)Se(2) (CIGS) nanoparticles, which have achieved impressive efficiencies. Despite these efficiencies, CdTe and CIGS are not amenable to large-scale production because of the cost and scarcity of Te, In, and Ga. Cu(2)ZnSnS(4) (CZTS), however, is an emerging solar cell material that contains only earth-abundant elements and has a near-optimal direct band gap of 1.45-1.65 eV and a large absorption coefficient. Here we report the direct synthesis of CZTS nanocrystals using the hot-injection method. In-depth characterization indicated that pure stoichiometric CZTS nanocrystals with an average particle size of 12.8 +/- 1.8 nm were formed. Optical measurements showed a band gap of 1.5 eV, which is optimal for a single-junction solar device.

Stoichiometric copper(I) selenide nanoparticles have been synthesized using the hot injection method. The effects of air exposure on the surface composition, crystal structure, and electronic properties were monitored using X-ray photoelectron spectroscopy, X-ray diffraction, and conductivity measurements. The current-voltage response changes from semiconducting to ohmic, and within a week a 3000-fold increase in conductivity is observed under ambient conditions. The enhanced electronic properties can be explained by the oxidation of Cu(+) and Se(2-) on the nanoparticle surface, ultimately leading to a solid-state conversion of the core from monoclinic Cu(2)Se to cubic Cu(1.8)Se. This behavior is a result of the facile solid-state ionic conductivity of cationic Cu within the crystal and the high susceptibility of the nanoparticle surface to oxidation. This regulated transformation is appealing as one could envision using layers of Cu(2)Se nanoparticles as both semiconducting and conducting domains in optoelectronic devices simply by tuning the electronic properties for each layer through controlled oxidation.

Hematite photoanodes were coated with an ultrathin cobalt oxide layer by atomic layer deposition (ALD). The optimal coating-1 ALD cycle, which amounts to <1 monolayer of Co(OH)2/Co3O4-resulted in significantly enhanced photoelectrochemical water oxidation performance. A stable, 100-200 mV cathodic shift in the photocurrent onset potential was observed that is correlated to an order of magnitude reduction in the resistance to charge transfer at the Fe2O3/H2O interface. Furthermore, the optical transparency of the ultrathin Co(OH)2/Co3O4 coating establishes it as a particularly advantageous treatment for nanostructured water oxidation photoanodes. The photocurrent of catalyst-coated nanostructured inverse opal scaffold hematite photoanodes reached 0.81 and 2.1 mA/cm(2) at 1.23 and 1.53 V, respectively.

Nanocrystals of multicomponent chalcogenides, such as Cu(2)ZnSnS(4) (CZTS), are potential building blocks for low-cost thin-film photovoltaics (PVs). CZTS PV devices with modest efficiencies have been realized through postdeposition annealing at high temperatures in Se vapor. However, little is known about the precise role of Se in the CZTS system. We report the direct solution-phase synthesis and characterization of Cu(2)ZnSn(S(1-x)Se(x))(4) nanocrystals (0 ≤ x ≤ 1) with the aim of probing the role of Se incorporation into CZTS. Our results indicate that increasing the amount of Se increases the lattice parameters, slightly decreases the band gap, and most importantly increases the electrical conductivity of the nanocrystals without a need for annealing.