In this Letter, the mechanism of double forming process phenomenon revealing in ZrO2/HfO2 bilayer resistive random access memory structure is investigated. This phenomenon caused by the formation of TiON interfacial layer can be well explained by using the energy band diagram. The TiON interfacial layer will be a tunneling barrier during the first forming process when a negative voltage applied on the device, while it will breakdown when applying a positive voltage. Besides, due to the double forming process, an asymmetric conductive filament with narrower size at ZrO2/HfO2 interface is formed in the device. The point for formation and rupture of the conductive filament can be confined at the ZrO2/HfO2 interface, and it will suppress the consumption of oxygen ions during endurance test. Therefore, high speed (40 ns) and large endurance (107 cycles) characteristics are achieved in this device structure.
The resistive switching characteristics of indium tin oxide (ITO)/Zn1−xCoxO/ITO transparent resistive memory devices were investigated. An appropriate amount of cobalt dopant in ZnO resistive layer demonstrated sufficient memory window and switching stability. In contrast, pure ZnO devices demonstrated a poor memory window, and using an excessive dopant concentration led to switching instability. To achieve suitable memory performance, relying only on controlling defect concentrations is insufficient; the grain growth orientation of the resistive layer must also be considered. Stable endurance with an ON/OFF ratio of more than one order of magnitude during 5000 cycles confirmed that the Co-doped ZnO device is a suitable candidate for resistive random access memory application. Additionally, fully transparent devices with a high transmittance of up to 90% at wavelength of 550 nm have been fabricated.
The effect of a defect concentration-modified top electrode on the bipolar resistance switching of transparent Al-doped ZnO/ZnO/ITO [AZO(TE)/ZnO/ITO(BE)] devices was investigated. Different oxygen vacancy concentrations in the top electrode, Al-doped ZnO, can be simply controlled by modulating the sputtering working pressure condition from 1.2 to 12 mTorr. The oxygen vacancy concentration between AZO and ZnO may trigger oxygen diffusion at the interface and affect the switching characteristic. High oxygen release from a ZnO resistive layer caused by excessive oxygen vacancy concentration at the top electrode is responsible for reducing the memory window as a result of reduced oxygen available to rupture the filament. Top electrode based on lower oxygen vacancy concentration has a higher memory window and an asymmetric resistive switching characteristic. However, all set of devices have excellent endurance of more than 10 4 cycles. This study showed that an Al-doped ZnO top electrode helps not only to achieve a transparent device but also to enhance memory properties by providing a suitable oxygen vacancy concentration.
In this study, the switching properties of an indium tin oxide (ITO)/zirconium oxide (ZrO2)/ITO single layer device and those of a device with an aluminum oxynitride (AlON) layer were investigated. The devices with highly transparent characteristics were fabricated. Compared with the ITO/ZrO2/ITO single layer device, the ITO/ZrO2/AlON/ITO bilayer device exhibited a larger ON/OFF ratio, higher endurance performance, and superior retention properties by using a simple two-step forming process. These substantial improvements in the resistive switching properties were attributed to the minimized influence of oxygen migration through the ITO top electrode (TE), which can be realized by forming an asymmetrical conductive filament with the weakest part at the ZrO2/AlON interface. Therefore, in the ITO/ZrO2/AlON/ITO bilayer device, the regions where conductive filament formation and rupture occur can be effectively moved from the TE interface to the interior of the device.
The influence of single and double forming on the switching stability of AZO/ZnO1−x/ITO transparent resistive memory devices was investigated. Devices that underwent single forming exhibited severe switching instability, where as those that underwent double forming exhibited excellent switching uniformity. The quantity of conducting filaments can be limited by applying the two-step forming process. Consequently, the set/reset process can be controlled, enhancing switching stability. Satisfactory endurance with an acceptable ON/OFF ratio of 102 and satisfactory retention behavior of 104 s at room temperature confirmed the reliability of optimized devices. Furthermore, highly transparent devices (transparency of approximately 85% in visible range) have been fabricated.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.